Allgemein
Property | Value | Comment |
---|---|---|
Dichte | 2.75 - 2.84 g/cm³ Show Material materials with Dichte of 2.75 - 2.84 g/cm³ | Typical for Wrought 2000 Series Aluminium |
Mechanisch
Property | Value | Condition | Related Standards | Comment |
---|---|---|---|---|
Elastizitätsmodul | 70.0 - 73.0 GPa Show Material materials with Elastizitätsmodul of 70.0 - 73.0 GPa | Typical for Wrought 2000 Series Aluminium | ||
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 2000 Series Aluminium | ||
Poissonzahl | 0.33 [-] Show Material materials with Poissonzahl of 0.33 [-] | Typical for Wrought 2000 Series Aluminium | ||
Schubmodule | 26.0 - 27.5 GPa Show Material materials with Schubmodule of 26.0 - 27.5 GPa | Typical for Wrought 2000 Series Aluminium | ||
Zugfestigkeit | 170.0 - 220.0 MPa Show Material materials with Zugfestigkeit of 170.0 - 220.0 MPa | H13 | AA Standards, ASTM B316 |
Thermisch
Property | Value | Comment |
---|---|---|
Koeffizient der thermischen Ausdehnung | 1.6e-05 - 2.4e-05 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 1.6e-05 - 2.4e-05 1/K | Typical for Wrought 2000 Series Aluminium |
Schmelzpunkt | 500.0 - 650.0 °C Show Material materials with Schmelzpunkt of 500.0 - 650.0 °C | Typical for Wrought 2000 Series Aluminium |
Spezifische Wärmekapazität | 816.0 - 963.0 J/(kg·K) Show Material materials with Spezifische Wärmekapazität of 816.0 - 963.0 J/(kg·K) | Typical for Wrought 2000 Series Aluminium |
Wärmeleitfähigkeit | 112.0 - 251.0 W/(m·K) Show Material materials with Wärmeleitfähigkeit of 112.0 - 251.0 W/(m·K) | Typical for Wrought 2000 Series Aluminium |
Elektrisch
Property | Value | Comment |
---|---|---|
Elektrische Leitfähigkeit | 18000000.0 - 30000000.0 S/m Show Material materials with Elektrische Leitfähigkeit of 18000000.0 - 30000000.0 S/m | Typical for Wrought 2000 Series Aluminium |
spezifischer Widerstand | 3.4e-08 - 6e-08 Ω·m Show Material materials with spezifischer Widerstand of 3.4e-08 - 6e-08 Ω·m | Typical for Wrought 2000 Series Aluminium |
Chemical properties
Property | Value | Condition | Related Standards |
---|---|---|---|
Chrom | 0.1 % Show Material materials with Chrom of 0.1 % | H13 | AA Standards, ASTM B316 |
Eisen | 0.70 % Show Material materials with Eisen of 0.70 % | H13 | AA Standards, ASTM B316 |
Kupfer | 2.2 - 3.0 % Show Material materials with Kupfer of 2.2 - 3.0 % | H13 | AA Standards, ASTM B316 |
Magnesium | 0.2 - 0.5 % Show Material materials with Magnesium of 0.2 - 0.5 % | H13 | AA Standards, ASTM B316 |
Mangan | 0.2 % Show Material materials with Mangan of 0.2 % | H13 | AA Standards, ASTM B316 |
Silizium | 0.8 % Show Material materials with Silizium of 0.8 % | H13 | AA Standards, ASTM B316 |
Zink | 0.25 % Show Material materials with Zink of 0.25 % | H13 | AA Standards, ASTM B316 |
Technological properties
Property | ||
---|---|---|
Brazing | general: no brazing is known or developed | |
Corrosion properties | Stress corrosion cracking: no damage during operation and laboratory tests, general: acceptable, in principle it should be protected | |
General machinability | General: sufficient | |
Workability | general (condition): acceptable |