Eigenschaften
Allgemein
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Dichte | 2.66 g/cm³ Show Material materials with Dichte of 2.66 g/cm³ | H34 | AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B547 |
Mechanisch
| Property | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|
Elastizitätsmodul | 71.0 GPa Show Material materials with Elastizitätsmodul of 71.0 GPa | H34 | AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B547 | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 5000 Series Aluminium | ||
Poissonzahl | 0.33 [-] Show Material materials with Poissonzahl of 0.33 [-] | Typical for Wrought 5000 Series Aluminium | ||
Schubmodule | 26.0 - 26.5 GPa Show Material materials with Schubmodule of 26.0 - 26.5 GPa | Typical for Wrought 5000 Series Aluminium | ||
Zugfestigkeit | 300.0 - 350.0 MPa Show Material materials with Zugfestigkeit of 300.0 - 350.0 MPa | H34 | AA Standards, ASTM B209, ASTM B313, ASTM B547 | |
300.0 MPa Show Material materials with Zugfestigkeit of 300.0 MPa | H34 | AA Standards, ASTM B210 | ||
325.0 MPa Show Material materials with Zugfestigkeit of 325.0 MPa | H34 | AA Standards |
Thermisch
| Property | Temperature | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|---|
Koeffizient der thermischen Ausdehnung | 20 °C | 2.38e-05 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 2.38e-05 1/K | H34 | AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B547 | |
100 °C | 2.38e-05 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 2.38e-05 1/K | H34 | AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B547 | ||
Max. Betriebstemperatur | 150.0 °C Show Material materials with Max. Betriebstemperatur of 150.0 °C | Typical for Wrought 5000 Series Aluminium | |||
Schmelzpunkt | 585.0 - 640.0 °C Show Material materials with Schmelzpunkt of 585.0 - 640.0 °C | H34 | AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B547 | ||
Spezifische Wärmekapazität | 879.0 - 963.0 J/(kg·K) Show Material materials with Spezifische Wärmekapazität of 879.0 - 963.0 J/(kg·K) | Typical for Wrought 5000 Series Aluminium | |||
Wärmeleitfähigkeit | 126 W/(m·K) Show Material materials with Wärmeleitfähigkeit of 126 W/(m·K) | H34 | AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B547 |
Elektrisch
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Elektrische Leitfähigkeit | 18000000.0 S/m Show Material materials with Elektrische Leitfähigkeit of 18000000.0 S/m | H34 | AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B547 |
spezifischer Widerstand | 5.56e-08 Ω·m Show Material materials with spezifischer Widerstand of 5.56e-08 Ω·m | H34 | AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B547 |
Chemical properties
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Chrom | 0.05 - 0.25 % Show Material materials with Chrom of 0.05 - 0.25 % | H34 | AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B547 |
Eisen | 0.50 % Show Material materials with Eisen of 0.50 % | H34 | AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B547 |
Kupfer | 0.1 % Show Material materials with Kupfer of 0.1 % | H34 | AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B547 |
Magnesium | 3.5 - 4.5 % Show Material materials with Magnesium of 3.5 - 4.5 % | H34 | AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B547 |
Mangan | 0.2 - 0.7 % Show Material materials with Mangan of 0.2 - 0.7 % | H34 | AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B547 |
Silizium | 0.4 % Show Material materials with Silizium of 0.4 % | H34 | AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B547 |
Titan | 0.15 % Show Material materials with Titan of 0.15 % | H34 | AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B547 |
Zink | 0.25 % Show Material materials with Zink of 0.25 % | H34 | AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B547 |
Technological properties
| Property | ||
|---|---|---|
| Brazing | general: no brazing is known or developed | |
| Corrosion properties | Stress corrosion cracking: no damage during operation and laboratory tests (O, H32, H116, H111), no damage during operation, limited damage during laboratory tests (H34, H36, H38), general: very good, without protection in industrial or seawater atmosphere | |
| General machinability | General: poor (O, H32, H116, H111), sufficient (H34, H36, H38) | |
| Workability | general (condition): good (O), acceptable (H32, H116, H111), poor(H36, H38) | |