Eigenschaften
Allgemein
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Dichte | 2.68 g/cm³ Show Material materials with Dichte of 2.68 g/cm³ | T6 | AA Standards, ASTM B247 |
Mechanisch
| Property | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|
Bending Fatigue Strength | 110.0 MPa Show Material materials with Bending Fatigue Strength of 110.0 MPa | T6 | AA Standards | |
Elastizitätsmodul | 79.0 GPa Show Material materials with Elastizitätsmodul of 79.0 GPa | T6 | AA Standards, ASTM B247 | |
Härte, Brinell | 120.0 [-] Show Material materials with Härte, Brinell of 120.0 [-] | T6 | AA Standards | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 4000 Series Aluminium | ||
Poissonzahl | 0.33 [-] Show Material materials with Poissonzahl of 0.33 [-] | Typical for Wrought 4000 Series Aluminium | ||
Schubmodule | 26.0 GPa Show Material materials with Schubmodule of 26.0 GPa | Typical for Wrought 4000 Series Aluminium | ||
Zugfestigkeit | 360.0 MPa Show Material materials with Zugfestigkeit of 360.0 MPa | T6 | AA Standards, ASTM B247 | |
380.0 MPa Show Material materials with Zugfestigkeit of 380.0 MPa | T6 | AA Standards |
Thermisch
| Property | Temperature | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|---|
Koeffizient der thermischen Ausdehnung | 20 °C | 1.9399999999999997e-05 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 1.9399999999999997e-05 1/K | T6 | AA Standards, ASTM B247 | |
100 °C | 1.9399999999999997e-05 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 1.9399999999999997e-05 1/K | T6 | AA Standards, ASTM B247 | ||
Schmelzpunkt | 530.0 - 570.0 °C Show Material materials with Schmelzpunkt of 530.0 - 570.0 °C | T6 | AA Standards, ASTM B247 | ||
Spezifische Wärmekapazität | 864.0 J/(kg·K) Show Material materials with Spezifische Wärmekapazität of 864.0 J/(kg·K) | Typical for Wrought 4000 Series Aluminium | |||
Wärmeleitfähigkeit | 138.0 - 155.0 W/(m·K) Show Material materials with Wärmeleitfähigkeit of 138.0 - 155.0 W/(m·K) | T6 | AA Standards, ASTM B247 |
Elektrisch
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Elektrische Leitfähigkeit | 20000000.0 - 23000000.0 S/m Show Material materials with Elektrische Leitfähigkeit of 20000000.0 - 23000000.0 S/m | T6 | AA Standards, ASTM B247 |
spezifischer Widerstand | 4.35e-08 - 5e-08 Ω·m Show Material materials with spezifischer Widerstand of 4.35e-08 - 5e-08 Ω·m | T6 | AA Standards, ASTM B247 |
Chemical properties
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Chrom | 0.1 % Show Material materials with Chrom of 0.1 % | T6 | AA Standards, ASTM B247 |
Eisen | 1.00 % Show Material materials with Eisen of 1.00 % | T6 | AA Standards, ASTM B247 |
Kupfer | 0.5 - 1.3 % Show Material materials with Kupfer of 0.5 - 1.3 % | T6 | AA Standards, ASTM B247 |
Magnesium | 0.8 - 1.3 % Show Material materials with Magnesium of 0.8 - 1.3 % | T6 | AA Standards, ASTM B247 |
Nickel | 0.5 - 1.3 % Show Material materials with Nickel of 0.5 - 1.3 % | T6 | AA Standards, ASTM B247 |
Silizium | 11.0 - 13.5 % Show Material materials with Silizium of 11.0 - 13.5 % | T6 | AA Standards, ASTM B247 |
Zink | 0.25 % Show Material materials with Zink of 0.25 % | T6 | AA Standards, ASTM B247 |
Technological properties
| Property | ||
|---|---|---|
| Brazing | general: no brazing is known or developed | |
| Corrosion properties | Stress corrosion cracking: no damage during operation, limited damage during laboratory tests, general: acceptable, in principle it should be protected | |
| General machinability | General: good to acceptable | |
| Workability | Moderate Workability | |