Property | Value | Condition | Related Standards |
---|---|---|---|
Dichte | 2.66 g/cm³ Show Material materials with Dichte of 2.66 g/cm³ | O | AA Standards, ASTM B209, ASTM B210, ASTM B221, ASTM B241 |
Mechanisch
Property | Value | Condition | Related Standards | Comment |
---|---|---|---|---|
Elastizitätsmodul | 71.0 GPa Show Material materials with Elastizitätsmodul of 71.0 GPa | O | AA Standards, ASTM B209, ASTM B210, ASTM B221, ASTM B241 | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 5000 Series Aluminium | ||
Poissonzahl | 0.33 [-] Show Material materials with Poissonzahl of 0.33 [-] | Typical for Wrought 5000 Series Aluminium | ||
Schubmodule | 26.0 - 26.5 GPa Show Material materials with Schubmodule of 26.0 - 26.5 GPa | Typical for Wrought 5000 Series Aluminium | ||
Zugfestigkeit | 265.0 MPa Show Material materials with Zugfestigkeit of 265.0 MPa | O | AA Standards, ASTM B209 | |
270.0 MPa Show Material materials with Zugfestigkeit of 270.0 MPa | O | AA Standards, ASTM B209 | ||
275.0 MPa Show Material materials with Zugfestigkeit of 275.0 MPa | O | AA Standards, ASTM B209 | ||
285.0 - 360.0 MPa Show Material materials with Zugfestigkeit of 285.0 - 360.0 MPa | O | AA Standards, ASTM B209 | ||
285.0 - 365.0 MPa Show Material materials with Zugfestigkeit of 285.0 - 365.0 MPa | O | AA Standards, ASTM B210, ASTM B221, ASTM B241 | ||
290.0 - 365.0 MPa Show Material materials with Zugfestigkeit of 290.0 - 365.0 MPa | O | AA Standards, ASTM B209 | ||
310.0 MPa Show Material materials with Zugfestigkeit of 310.0 MPa | O | AA Standards |
Thermisch
Property | Temperature | Value | Condition | Related Standards | Comment |
---|---|---|---|---|---|
Koeffizient der thermischen Ausdehnung | 20 °C | 2.3899999999999998e-05 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 2.3899999999999998e-05 1/K | O | AA Standards, ASTM B209, ASTM B210, ASTM B221, ASTM B241 | |
100 °C | 2.3899999999999998e-05 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 2.3899999999999998e-05 1/K | O | AA Standards, ASTM B209, ASTM B210, ASTM B221, ASTM B241 | ||
Max. Betriebstemperatur | 150.0 °C Show Material materials with Max. Betriebstemperatur of 150.0 °C | Typical for Wrought 5000 Series Aluminium | |||
Schmelzpunkt | 570.0 - 640.0 °C Show Material materials with Schmelzpunkt of 570.0 - 640.0 °C | O | AA Standards, ASTM B209, ASTM B210, ASTM B221, ASTM B241 | ||
Spezifische Wärmekapazität | 879.0 - 963.0 J/(kg·K) Show Material materials with Spezifische Wärmekapazität of 879.0 - 963.0 J/(kg·K) | Typical for Wrought 5000 Series Aluminium | |||
Wärmeleitfähigkeit | 117.0 Show Material materials with Wärmeleitfähigkeit of 117.0 | O | AA Standards, ASTM B209, ASTM B210, ASTM B221, ASTM B241 |
Elektrisch
Property | Value | Condition | Related Standards |
---|---|---|---|
Elektrische Leitfähigkeit | 17000000.0 S/m Show Material materials with Elektrische Leitfähigkeit of 17000000.0 S/m | O | AA Standards, ASTM B209, ASTM B210, ASTM B221, ASTM B241 |
spezifischer Widerstand | 5.88e-08 Ω·m Show Material materials with spezifischer Widerstand of 5.88e-08 Ω·m | O | AA Standards, ASTM B209, ASTM B210, ASTM B221, ASTM B241 |
Chemical properties
Property | Value | Condition | Related Standards |
---|---|---|---|
Chrom | 0.05 - 0.2 % Show Material materials with Chrom of 0.05 - 0.2 % | O | AA Standards, ASTM B209, ASTM B210, ASTM B221, ASTM B241 |
Eisen | 0.40 % Show Material materials with Eisen of 0.40 % | O | AA Standards, ASTM B209, ASTM B210, ASTM B221, ASTM B241 |
Kupfer | 0.1 % Show Material materials with Kupfer of 0.1 % | O | AA Standards, ASTM B209, ASTM B210, ASTM B221, ASTM B241 |
Magnesium | 4.7 - 5.5 % Show Material materials with Magnesium of 4.7 - 5.5 % | O | AA Standards, ASTM B209, ASTM B210, ASTM B221, ASTM B241 |
Mangan | 0.5 - 1.0 % Show Material materials with Mangan of 0.5 - 1.0 % | O | AA Standards, ASTM B209, ASTM B210, ASTM B221, ASTM B241 |
Silizium | 0.25 % Show Material materials with Silizium of 0.25 % | O | AA Standards, ASTM B209, ASTM B210, ASTM B221, ASTM B241 |
Titan | 0.2 % Show Material materials with Titan of 0.2 % | O | AA Standards, ASTM B209, ASTM B210, ASTM B221, ASTM B241 |
Zink | 0.25 % Show Material materials with Zink of 0.25 % | O | AA Standards, ASTM B209, ASTM B210, ASTM B221, ASTM B241 |
Technological properties
Property | ||
---|---|---|
Brazing | general: no brazing is known or developed | |
Corrosion properties | Stress corrosion cracking: no damage during operation, limited damage during laboratory tests, general: very good, without protection in industrial or seawater atmosphere | |
General machinability | General: poor (O, H321, H116) | |
Workability | general (condition): acceptable (O), poor(H321, H116) |