Allgemein
Property | Value | Condition | Related Standards |
---|---|---|---|
Dichte | 2.72 g/cm³ Show Material materials with Dichte of 2.72 g/cm³ | T62 | AA Standards, ASTM B221, ASTM B241 |
Mechanisch
Property | Value | Condition | Related Standards | Comment |
---|---|---|---|---|
Elastizitätsmodul | 69.0 GPa Show Material materials with Elastizitätsmodul of 69.0 GPa | T62 | AA Standards, ASTM B221, ASTM B241 | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 6000 Series Aluminium | ||
Poissonzahl | 0.33 [-] Show Material materials with Poissonzahl of 0.33 [-] | Typical for Wrought 6000 Series Aluminium | ||
Schubmodule | 26.0 - 26.5 GPa Show Material materials with Schubmodule of 26.0 - 26.5 GPa | Typical for Wrought 6000 Series Aluminium | ||
Zugfestigkeit | 345.0 MPa Show Material materials with Zugfestigkeit of 345.0 MPa | T62 | AA Standards, ASTM B221, ASTM B241 |
Thermisch
Property | Temperature | Value | Condition | Related Standards | Comment |
---|---|---|---|---|---|
Koeffizient der thermischen Ausdehnung | 20 °C | 2.3199999999999998e-05 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 2.3199999999999998e-05 1/K | T62 | AA Standards, ASTM B221, ASTM B241 | |
100 °C | 2.3199999999999998e-05 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 2.3199999999999998e-05 1/K | T62 | AA Standards, ASTM B221, ASTM B241 | ||
Schmelzpunkt | 560.0 - 645.0 °C Show Material materials with Schmelzpunkt of 560.0 - 645.0 °C | T62 | AA Standards, ASTM B221, ASTM B241 | ||
Spezifische Wärmekapazität | 887.0 - 963.0 J/(kg·K) Show Material materials with Spezifische Wärmekapazität of 887.0 - 963.0 J/(kg·K) | Typical for Wrought 6000 Series Aluminium | |||
Wärmeleitfähigkeit | 146.0 - 155.0 W/(m·K) Show Material materials with Wärmeleitfähigkeit of 146.0 - 155.0 W/(m·K) | T62 | AA Standards, ASTM B221, ASTM B241 |
Elektrisch
Property | Value | Condition | Related Standards |
---|---|---|---|
Elektrische Leitfähigkeit | 21000000.0 - 23000000.0 S/m Show Material materials with Elektrische Leitfähigkeit of 21000000.0 - 23000000.0 S/m | T62 | AA Standards, ASTM B221, ASTM B241 |
spezifischer Widerstand | 4.35e-08 - 4.76e-08 Ω·m Show Material materials with spezifischer Widerstand of 4.35e-08 - 4.76e-08 Ω·m | T62 | AA Standards, ASTM B221, ASTM B241 |
Chemical properties
Property | Value | Condition | Related Standards |
---|---|---|---|
Chrom | 0.4 % Show Material materials with Chrom of 0.4 % | T62 | AA Standards, ASTM B221, ASTM B241 |
Eisen | 0.50 % Show Material materials with Eisen of 0.50 % | T62 | AA Standards, ASTM B221, ASTM B241 |
Kupfer | 0.7 - 1.2 % Show Material materials with Kupfer of 0.7 - 1.2 % | T62 | AA Standards, ASTM B221, ASTM B241 |
Magnesium | 0.8 - 1.4 % Show Material materials with Magnesium of 0.8 - 1.4 % | T62 | AA Standards, ASTM B221, ASTM B241 |
Mangan | 0.6 - 1.1 % Show Material materials with Mangan of 0.6 - 1.1 % | T62 | AA Standards, ASTM B221, ASTM B241 |
Silizium | 0.9 - 1.8 % Show Material materials with Silizium of 0.9 - 1.8 % | T62 | AA Standards, ASTM B221, ASTM B241 |
Titan | 0.2 % Show Material materials with Titan of 0.2 % | T62 | AA Standards, ASTM B221, ASTM B241 |
Zink | 0.25 % Show Material materials with Zink of 0.25 % | T62 | AA Standards, ASTM B221, ASTM B241 |
Technological properties
Property | ||
---|---|---|
Brazing | general: no brazing is known or developed | |
Corrosion properties | Stress corrosion cracking: no damage during operation and laboratory tests (O), no damage during operation, limited damage during laboratory tests, general: good, without protection in industrial or seawater atmosphere | |
General machinability | General: poor (O), sufficient (T4, T4510, T4511), good to acceptable (T6, T6510, T6511) | |
Workability | general (condition): acceptable (O), poor(T4, T4510, T4511, T6, T6510, T6511) |