Eigenschaften
Allgemein
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Dichte | 2.72 g/cm³ Show Material materials with Dichte of 2.72 g/cm³ | T9 | AA Standards, ASTM B210, ASTM B211, ASTM B483 |
Mechanisch
| Property | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|
Bending Fatigue Strength | 90.0 MPa Show Material materials with Bending Fatigue Strength of 90.0 MPa | T9 | AA Standards | |
Elastizitätsmodul | 70.0 GPa Show Material materials with Elastizitätsmodul of 70.0 GPa | Typical for Wrought 6000 Series Aluminium | ||
Härte, Brinell | 120.0 [-] Show Material materials with Härte, Brinell of 120.0 [-] | T9 | AA Standards | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 6000 Series Aluminium | ||
Poissonzahl | 0.33 [-] Show Material materials with Poissonzahl of 0.33 [-] | Typical for Wrought 6000 Series Aluminium | ||
Schubmodule | 26.0 - 26.5 GPa Show Material materials with Schubmodule of 26.0 - 26.5 GPa | Typical for Wrought 6000 Series Aluminium | ||
Zugfestigkeit | 330.0 MPa Show Material materials with Zugfestigkeit of 330.0 MPa | T9 | AA Standards, ASTM B210, ASTM B483 | |
345.0 MPa Show Material materials with Zugfestigkeit of 345.0 MPa | T9 | AA Standards, ASTM B211 | ||
360.0 MPa Show Material materials with Zugfestigkeit of 360.0 MPa | T9 | AA Standards, ASTM B211 | ||
400.0 MPa Show Material materials with Zugfestigkeit of 400.0 MPa | T9 | AA Standards |
Thermisch
| Property | Temperature | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|---|
Koeffizient der thermischen Ausdehnung | 20 °C | 2.3399999999999996e-05 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 2.3399999999999996e-05 1/K | T9 | AA Standards, ASTM B210, ASTM B211, ASTM B483 | |
100 °C | 2.3399999999999996e-05 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 2.3399999999999996e-05 1/K | T9 | AA Standards, ASTM B210, ASTM B211, ASTM B483 | ||
Schmelzpunkt | 580.0 - 650.0 °C Show Material materials with Schmelzpunkt of 580.0 - 650.0 °C | T9 | AA Standards, ASTM B210, ASTM B211, ASTM B483 | ||
Spezifische Wärmekapazität | 887.0 - 963.0 J/(kg·K) Show Material materials with Spezifische Wärmekapazität of 887.0 - 963.0 J/(kg·K) | Typical for Wrought 6000 Series Aluminium | |||
Wärmeleitfähigkeit | 172 W/(m·K) Show Material materials with Wärmeleitfähigkeit of 172 W/(m·K) | T9 | AA Standards, ASTM B210, ASTM B211, ASTM B483 |
Elektrisch
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Elektrische Leitfähigkeit | 26000000.0 S/m Show Material materials with Elektrische Leitfähigkeit of 26000000.0 S/m | T9 | AA Standards, ASTM B210, ASTM B211, ASTM B483 |
spezifischer Widerstand | 3.85e-08 Ω·m Show Material materials with spezifischer Widerstand of 3.85e-08 Ω·m | T9 | AA Standards, ASTM B210, ASTM B211, ASTM B483 |
Chemical properties
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Bismut | 0.4 - 0.7 % Show Material materials with Bismut of 0.4 - 0.7 % | T9 | AA Standards, ASTM B210, ASTM B211, ASTM B483 |
Blei | 0.4 - 0.7 % Show Material materials with Blei of 0.4 - 0.7 % | T9 | AA Standards, ASTM B210, ASTM B211, ASTM B483 |
Chrom | 0.04 - 0.14 % Show Material materials with Chrom of 0.04 - 0.14 % | T9 | AA Standards, ASTM B210, ASTM B211, ASTM B483 |
Eisen | 0.70 % Show Material materials with Eisen of 0.70 % | T9 | AA Standards, ASTM B210, ASTM B211, ASTM B483 |
Kupfer | 0.15 - 0.4 % Show Material materials with Kupfer of 0.15 - 0.4 % | T9 | AA Standards, ASTM B210, ASTM B211, ASTM B483 |
Magnesium | 0.8 - 1.2 % Show Material materials with Magnesium of 0.8 - 1.2 % | T9 | AA Standards, ASTM B210, ASTM B211, ASTM B483 |
Mangan | 0.15 % Show Material materials with Mangan of 0.15 % | T9 | AA Standards, ASTM B210, ASTM B211, ASTM B483 |
Silizium | 0.4 - 0.8 % Show Material materials with Silizium of 0.4 - 0.8 % | T9 | AA Standards, ASTM B210, ASTM B211, ASTM B483 |
Titan | 0.15 % Show Material materials with Titan of 0.15 % | T9 | AA Standards, ASTM B210, ASTM B211, ASTM B483 |
Zink | 0.25 % Show Material materials with Zink of 0.25 % | T9 | AA Standards, ASTM B210, ASTM B211, ASTM B483 |
Technological properties
| Property | ||
|---|---|---|
| Brazing | general: Lötbar mit speziellen Techniken oder bei bestimmten Anwendungen | |
| Corrosion properties | Stress corrosion cracking: no damage during operation and laboratory tests, general: good, without protection in industrial or seawater atmosphere | |
| General machinability | General: good to acceptable (T6, T651, T6510, T6511, T9) | |
| Workability | general (condition): poor(T6, T651, T6510, T6511), not suitable (T9) | |