Eigenschaften
Allgemein
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Dichte | 2.83 g/cm³ Show Material materials with Dichte of 2.83 g/cm³ | T6 | AA Standards, ASTM B209, ASTM B221, ASTM B241, ASTM B316 |
Mechanisch
| Property | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|
Elastizitätsmodul | 72.0 GPa Show Material materials with Elastizitätsmodul of 72.0 GPa | T6 | AA Standards, ASTM B209, ASTM B221, ASTM B241, ASTM B316 | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 7000 Series Aluminium | ||
Poissonzahl | 0.33 [-] Show Material materials with Poissonzahl of 0.33 [-] | Typical for Wrought 7000 Series Aluminium | ||
Schubmodule | 26.4 - 27.1 GPa Show Material materials with Schubmodule of 26.4 - 27.1 GPa | Typical for Wrought 7000 Series Aluminium | ||
Zugfestigkeit | 565.0 MPa Show Material materials with Zugfestigkeit of 565.0 MPa | T6 | AA Standards, ASTM B221, ASTM B241 | |
570.0 MPa Show Material materials with Zugfestigkeit of 570.0 MPa | T6 | AA Standards, ASTM B209 | ||
580.0 MPa Show Material materials with Zugfestigkeit of 580.0 MPa | T6 | AA Standards, ASTM B209, ASTM B221, ASTM B241, ASTM B316 | ||
595.0 MPa Show Material materials with Zugfestigkeit of 595.0 MPa | T6 | AA Standards, ASTM B221 | ||
600.0 MPa Show Material materials with Zugfestigkeit of 600.0 MPa | T6 | AA Standards, ASTM B221, ASTM B241 | ||
605.0 MPa Show Material materials with Zugfestigkeit of 605.0 MPa | T6 | AA Standards |
Thermisch
| Property | Temperature | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|---|
Koeffizient der thermischen Ausdehnung | 20 °C | 2.3399999999999996e-05 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 2.3399999999999996e-05 1/K | T6 | AA Standards, ASTM B209, ASTM B221, ASTM B241, ASTM B316 | |
100 °C | 2.3399999999999996e-05 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 2.3399999999999996e-05 1/K | T6 | AA Standards, ASTM B209, ASTM B221, ASTM B241, ASTM B316 | ||
Schmelzpunkt | 475.0 - 630.0 °C Show Material materials with Schmelzpunkt of 475.0 - 630.0 °C | T6 | AA Standards, ASTM B209, ASTM B221, ASTM B241, ASTM B316 | ||
Spezifische Wärmekapazität | 795.0 - 1050.0 J/(kg·K) Show Material materials with Spezifische Wärmekapazität of 795.0 - 1050.0 J/(kg·K) | Typical for Wrought 7000 Series Aluminium | |||
Wärmeleitfähigkeit | 126 W/(m·K) Show Material materials with Wärmeleitfähigkeit of 126 W/(m·K) | T6 | AA Standards, ASTM B209, ASTM B221, ASTM B241, ASTM B316 |
Elektrisch
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Elektrische Leitfähigkeit | 18000000.0 S/m Show Material materials with Elektrische Leitfähigkeit of 18000000.0 S/m | T6 | AA Standards, ASTM B209, ASTM B221, ASTM B241, ASTM B316 |
spezifischer Widerstand | 5.56e-08 Ω·m Show Material materials with spezifischer Widerstand of 5.56e-08 Ω·m | T6 | AA Standards, ASTM B209, ASTM B221, ASTM B241, ASTM B316 |
Chemical properties
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Chrom | 0.18 - 0.28 % Show Material materials with Chrom of 0.18 - 0.28 % | T6 | AA Standards, ASTM B209, ASTM B221, ASTM B241, ASTM B316 |
Eisen | 0.50 % Show Material materials with Eisen of 0.50 % | T6 | AA Standards, ASTM B209, ASTM B221, ASTM B241, ASTM B316 |
Kupfer | 1.6 - 2.4 % Show Material materials with Kupfer of 1.6 - 2.4 % | T6 | AA Standards, ASTM B209, ASTM B221, ASTM B241, ASTM B316 |
Magnesium | 2.4 - 3.1 % Show Material materials with Magnesium of 2.4 - 3.1 % | T6 | AA Standards, ASTM B209, ASTM B221, ASTM B241, ASTM B316 |
Mangan | 0.3 % Show Material materials with Mangan of 0.3 % | T6 | AA Standards, ASTM B209, ASTM B221, ASTM B241, ASTM B316 |
Silizium | 0.4 % Show Material materials with Silizium of 0.4 % | T6 | AA Standards, ASTM B209, ASTM B221, ASTM B241, ASTM B316 |
Titan | 0.2 % Show Material materials with Titan of 0.2 % | T6 | AA Standards, ASTM B209, ASTM B221, ASTM B241, ASTM B316 |
Zink | 6.3 - 7.3 % Show Material materials with Zink of 6.3 - 7.3 % | T6 | AA Standards, ASTM B209, ASTM B221, ASTM B241, ASTM B316 |
Technological properties
| Property | ||
|---|---|---|
| Brazing | general: no brazing is known or developed | |
| Corrosion properties | Stress corrosion cracking: Operational damage in areas with tensile stresses transverse to the grain structure, limited damage to laboratory samples, general: good, without protection in industrial or seawater atmosphere | |
| General machinability | General: good to acceptable | |
| Workability | general (condition): not suitable | |