Allgemein
Property | Value | Condition | Related Standards |
---|---|---|---|
Dichte | 2.7 g/cm³ Show Material materials with Dichte of 2.7 g/cm³ | T832 | AA Standards, ASTM B210, ASTM B483 |
Mechanisch
Property | Value | Condition | Related Standards | Comment |
---|---|---|---|---|
Elastizitätsmodul | 69.0 GPa Show Material materials with Elastizitätsmodul of 69.0 GPa | T832 | AA Standards, ASTM B210, ASTM B483 | |
Härte, Brinell | 95.0 [-] Show Material materials with Härte, Brinell of 95.0 [-] | T832 | AA Standards | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 6000 Series Aluminium | ||
Poissonzahl | 0.33 [-] Show Material materials with Poissonzahl of 0.33 [-] | Typical for Wrought 6000 Series Aluminium | ||
Schubmodule | 26.0 - 26.5 GPa Show Material materials with Schubmodule of 26.0 - 26.5 GPa | Typical for Wrought 6000 Series Aluminium | ||
Zugfestigkeit | 275.0 MPa Show Material materials with Zugfestigkeit of 275.0 MPa | T832 | AA Standards, ASTM B210, ASTM B483 | |
285.0 MPa Show Material materials with Zugfestigkeit of 285.0 MPa | T832 | AA Standards, ASTM B210, ASTM B483 | ||
290.0 MPa Show Material materials with Zugfestigkeit of 290.0 MPa | T832 | AA Standards |
Thermisch
Property | Temperature | Value | Condition | Related Standards | Comment |
---|---|---|---|---|---|
Koeffizient der thermischen Ausdehnung | 20 °C | 2.3399999999999996e-05 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 2.3399999999999996e-05 1/K | T832 | AA Standards, ASTM B210, ASTM B483 | |
100 °C | 2.3399999999999996e-05 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 2.3399999999999996e-05 1/K | T832 | AA Standards, ASTM B210, ASTM B483 | ||
Schmelzpunkt | 615.0 - 655.0 °C Show Material materials with Schmelzpunkt of 615.0 - 655.0 °C | T832 | AA Standards, ASTM B210, ASTM B483 | ||
Spezifische Wärmekapazität | 887.0 - 963.0 J/(kg·K) Show Material materials with Spezifische Wärmekapazität of 887.0 - 963.0 J/(kg·K) | Typical for Wrought 6000 Series Aluminium | |||
Wärmeleitfähigkeit | 193.0 - 218.0 W/(m·K) Show Material materials with Wärmeleitfähigkeit of 193.0 - 218.0 W/(m·K) | T832 | AA Standards, ASTM B210, ASTM B483 |
Elektrisch
Property | Value | Condition | Related Standards |
---|---|---|---|
Elektrische Leitfähigkeit | 29000000.0 - 34000000.0 S/m Show Material materials with Elektrische Leitfähigkeit of 29000000.0 - 34000000.0 S/m | T832 | AA Standards, ASTM B210, ASTM B483 |
spezifischer Widerstand | 2.94e-08 - 3.45e-08 Ω·m Show Material materials with spezifischer Widerstand of 2.94e-08 - 3.45e-08 Ω·m | T832 | AA Standards, ASTM B210, ASTM B483 |
Chemical properties
Property | Value | Condition | Related Standards |
---|---|---|---|
Chrom | 0.1 % Show Material materials with Chrom of 0.1 % | T832 | AA Standards, ASTM B210, ASTM B483 |
Eisen | 0.35 % Show Material materials with Eisen of 0.35 % | T832 | AA Standards, ASTM B210, ASTM B483 |
Kupfer | 0.1 % Show Material materials with Kupfer of 0.1 % | T832 | AA Standards, ASTM B210, ASTM B483 |
Magnesium | 0.45 - 0.9 % Show Material materials with Magnesium of 0.45 - 0.9 % | T832 | AA Standards, ASTM B210, ASTM B483 |
Mangan | 0.1 % Show Material materials with Mangan of 0.1 % | T832 | AA Standards, ASTM B210, ASTM B483 |
Silizium | 0.2 - 0.6 % Show Material materials with Silizium of 0.2 - 0.6 % | T832 | AA Standards, ASTM B210, ASTM B483 |
Titan | 0.1 % Show Material materials with Titan of 0.1 % | T832 | AA Standards, ASTM B210, ASTM B483 |
Zink | 0.1 % Show Material materials with Zink of 0.1 % | T832 | AA Standards, ASTM B210, ASTM B483 |
Technological properties
Property | ||
---|---|---|
Brazing | general: possible with commercial processes and methods | |
Corrosion properties | Stress corrosion cracking: no damage during operation and laboratory tests, general: very good, without protection in industrial or seawater atmosphere | |
General machinability | General: poor (T1, T4), sufficient (T5, T452, T6, T83, T831, T832) | |
Workability | general (condition): acceptable (T1, T4, T5, T452), poor(T6, T83, T831, T832) |