Eigenschaften
Allgemein
| Property | Temperature | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|---|
Dichte | 2.65 g/cm³ Show Material materials with Dichte of 2.65 g/cm³ | T64 | EN 1706 | Casting | |
20.0 °C | 2.65 g/cm³ Show Material materials with Dichte of 2.65 g/cm³ | T64 | EN 1706 |
Mechanisch
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
Bending Fatigue Strength | 80.0 - 110.0 MPa Show Material materials with Bending Fatigue Strength of 80.0 - 110.0 MPa | T64 | EN 1706 | Casting | ||
Elastizitätsmodul | 74.0 GPa Show Material materials with Elastizitätsmodul of 74.0 GPa | T64 | EN 1706 | Casting | ||
20.0 °C | 74.0 GPa Show Material materials with Elastizitätsmodul of 74.0 GPa | T64 | EN 1706 | |||
Härte, Brinell | 80.0 [-] Show Material materials with Härte, Brinell of 80.0 [-] | T64 | EN 1706 | Casting | ||
20.0 °C | 80.0 [-] Show Material materials with Härte, Brinell of 80.0 [-] | T64 | EN 1706 | |||
Poissonzahl | 0.33 [-] Show Material materials with Poissonzahl of 0.33 [-] | Typical for Cast 3xx.x Series Aluminium | ||||
Schubmodule | 2.8 GPa Show Material materials with Schubmodule of 2.8 GPa | Typical for Cast 3xx.x Series Aluminium | ||||
Zugfestigkeit | 240.0 MPa Show Material materials with Zugfestigkeit of 240.0 MPa | T64 | EN 1706 | Casting | ||
20.0 °C | 240.0 MPa Show Material materials with Zugfestigkeit of 240.0 MPa | T64 | EN 1706 | |||
20.0 °C | 250.0 MPa Show Material materials with Zugfestigkeit of 250.0 MPa | T64 | EN 1706 |
Thermisch
| Property | Temperature | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|---|
Koeffizient der thermischen Ausdehnung | 20 °C | 2.1e-05 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 2.1e-05 1/K | T64 | EN 1706 | Casting |
100.0 °C | 2.1e-05 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 2.1e-05 1/K | T64 | EN 1706 | Casting | |
100 °C | 2.1e-05 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 2.1e-05 1/K | T64 | EN 1706 | Casting | |
Schmelzpunkt | 550.0 - 600.0 °C Show Material materials with Schmelzpunkt of 550.0 - 600.0 °C | T64 | EN 1706 | Casting | |
Spezifische Wärmekapazität | 910.0 J/(kg·K) Show Material materials with Spezifische Wärmekapazität of 910.0 J/(kg·K) | T64 | EN 1706 | Casting | |
20.0 °C | 910.0 J/(kg·K) Show Material materials with Spezifische Wärmekapazität of 910.0 J/(kg·K) | T64 | EN 1706 | ||
Wärmeleitfähigkeit | 20.0 °C | 150.0 - 170.0 W/(m·K) Show Material materials with Wärmeleitfähigkeit of 150.0 - 170.0 W/(m·K) | T64 | EN 1706 | Casting |
Elektrisch
| Property | Temperature | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|---|
Elektrische Leitfähigkeit | 20.0 °C | 19000000.0 - 25000000.0 S/m Show Material materials with Elektrische Leitfähigkeit of 19000000.0 - 25000000.0 S/m | T64 | EN 1706 | Casting |
spezifischer Widerstand | 4e-08 - 5.26e-08 Ω·m Show Material materials with spezifischer Widerstand of 4e-08 - 5.26e-08 Ω·m | T64 | EN 1706 | Casting |
Chemical properties
| Property | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|
Aluminium | 86.95 % Show Material materials with Aluminium of 86.95 % | T64 | EN 1706 | |
Blei | 0.05 % Show Material materials with Blei of 0.05 % | T64 | EN 1706 | Casting |
Eisen | 0.55 % Show Material materials with Eisen of 0.55 % | T64 | EN 1706 | |
0.55 % Show Material materials with Eisen of 0.55 % | T64 | EN 1706 | Casting | |
Kupfer | 0.05 % Show Material materials with Kupfer of 0.05 % | T64 | EN 1706 | Casting |
Magnesium | 0.2 - 0.45 % Show Material materials with Magnesium of 0.2 - 0.45 % | T64 | EN 1706 | Casting |
Mangan | 0.45 % Show Material materials with Mangan of 0.45 % | T64 | EN 1706 | Casting |
Nickel | 0.05 % Show Material materials with Nickel of 0.05 % | T64 | EN 1706 | Casting |
Silizium | 9.0 - 11.0 % Show Material materials with Silizium of 9.0 - 11.0 % | T64 | EN 1706 | Casting |
Titan | 0.15 % Show Material materials with Titan of 0.15 % | T64 | EN 1706 | Casting |
Zink | 0.1 % Show Material materials with Zink of 0.1 % | T64 | EN 1706 | Casting |
Zinn | 0.05 % Show Material materials with Zinn of 0.05 % | T64 | EN 1706 | Casting |
Technological properties
| Property | ||
|---|---|---|
| Anodizing | decorative: not recommended | |
| Corrosion properties | general: good | |
| General machinability | after thermal treatment: good to acceptable, as cast: good | |
| Processing methods | permanent mould casting, separately cast test sample | |