EN 573-3 Grade 3.0526 O

Want to keep this datasheet? Save it now in your required format

Description

The alloy AlMn1Mg1 has similar properties like AlMn1, however it reaches higher strength (to F 26). It has also relatively high strength in the soft condition, but it is well cold fomrable. The alloy belongs to the nature-hard aluminum materials. A strength increase can be achieved, not by a purposeful heat treatment only by cold forming. It is very well warm and cold transformable and is suitable to the deep-drawing (no lappet formation). The alloy is very corrosion and sea water-steadily. The main field of application, the packing, determines the kind of semi-finished material standardized according to DIN 1788 and DIN 1745 (sheet metal and strip). Application: In the packing (DIN 59606) for cans (dose lower parts, abgestreckte doses), breaking covers and catches of all kinds. In the building industry for roofings (usually profile boards), claddings as well as for roll shutter and roll gates.

Related Standards

Equivalent Materials

Diese Materialdaten wurden von WIAM,AluKey zur Verfügung gestellt

Alle Daten beziehen sich auf Raumtemperatur soweit nicht anderweitig spezifiziert. SI Einheiten werden verwendt soweit nicht anderweitig spezifiziert.
Äquivalente Standards sind ähnlich zu einem oder mehreren Standards die der Anbieter angegeben hat. Manche äquivalente Standards können strikter sein oder außerhalb der Bedingungen des ursprünglichen Standards.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

All categories

Empfohlene Literatur

6061-T6 Aluminium – The Ultimate Guide

7075-T6 Aluminium: Overview & Properties

Aircraft Aluminium Grades

Cast vs. Wrought Aluminium: Standards, Properties and Applications

Precipitation Hardening (Age Hardening)

Alle anzeigen

Do you supply similar materials?

List your company on Matmatch now and reach engineers around the world looking for such materials.

Request more information

Eigenschaften

Allgemein

Property	Temperature	Value	Condition	Related Standards	Shape
Dichte		2.72 g/cm³ Show Material materials with Dichte of 2.72 g/cm³	O	EN 573-3, EN 485
	20.0 °C	2.72 g/cm³ Show Material materials with Dichte of 2.72 g/cm³	O	DIN 1725-1, EN 573-3, EN 573-4	Flat

Mechanisch

Property	Temperature	Value	Condition	Related Standards	Shape	Comment
Biegewinkel 180°		0.5 °/t Show Material materials with Biegewinkel 180° of 0.5 °/t	O	EN 573-3, EN 485
		1.0 °/t Show Material materials with Biegewinkel 180° of 1.0 °/t	O	EN 573-3, EN 485
Biegewinkel 90°		1.0 °/t Show Material materials with Biegewinkel 90° of 1.0 °/t	O	EN 573-3, EN 485
		2.0 °/t Show Material materials with Biegewinkel 90° of 2.0 °/t	O	EN 573-3, EN 485
Dehnung	-196.0 °C	38.0 % Show Material materials with Dehnung of 38.0 %	O	DIN 1725-1, EN 573-3, EN 573-4
	-80.0 °C	30.0 % Show Material materials with Dehnung of 30.0 %	O	DIN 1725-1, EN 573-3, EN 573-4
	-28.0 °C	26.0 % Show Material materials with Dehnung of 26.0 %	O	DIN 1725-1, EN 573-3, EN 573-4
		13.0 % Show Material materials with Dehnung of 13.0 %	O	EN 573-3, EN 485		A50
		14.0 % Show Material materials with Dehnung of 14.0 %	O	EN 573-3, EN 485		A100
		14.0 % Show Material materials with Dehnung of 14.0 %	O	EN 573-3, EN 485		A50
		15.0 % Show Material materials with Dehnung of 15.0 %	O	EN 573-3, EN 485		A50
		16.0 % Show Material materials with Dehnung of 16.0 %	O	EN 573-3, EN 485		A50
	20.0 °C	7.0 % Show Material materials with Dehnung of 7.0 %	O	DIN 1725-1, EN 573-3, EN 573-4	Flat	A100
	20.0 °C	10.0 % Show Material materials with Dehnung of 10.0 %	O	DIN 1725-1, EN 573-3, EN 573-4	Flat	A100
	20.0 °C	13.0 % Show Material materials with Dehnung of 13.0 %	O	DIN 1725-1, EN 573-3, EN 573-4	Flat	A100
	20.0 °C	15.0 % Show Material materials with Dehnung of 15.0 %	O	DIN 1725-1, EN 573-3, EN 573-4	Flat	A10
	20.0 °C	18.0 % Show Material materials with Dehnung of 18.0 %	O	DIN 1725-1, EN 573-3, EN 573-4	Flat
	20.0 °C	25.0 % Show Material materials with Dehnung of 25.0 %	O	DIN 1725-1, EN 573-3, EN 573-4
	100.0 °C	25.0 % Show Material materials with Dehnung of 25.0 %	O	DIN 1725-1, EN 573-3, EN 573-4
	150.0 °C	35.0 % Show Material materials with Dehnung of 35.0 %	O	DIN 1725-1, EN 573-3, EN 573-4
	200.0 °C	55.0 % Show Material materials with Dehnung of 55.0 %	O	DIN 1725-1, EN 573-3, EN 573-4
	260.0 °C	70.0 % Show Material materials with Dehnung of 70.0 %	O	DIN 1725-1, EN 573-3, EN 573-4
	315.0 °C	80.0 % Show Material materials with Dehnung of 80.0 %	O	DIN 1725-1, EN 573-3, EN 573-4
	370.0 °C	90.0 % Show Material materials with Dehnung of 90.0 %	O	DIN 1725-1, EN 573-3, EN 573-4
Elastizitätsmodul		69.0 GPa Show Material materials with Elastizitätsmodul of 69.0 GPa	O	EN 573-3, EN 485
		70.0 GPa Show Material materials with Elastizitätsmodul of 70.0 GPa	O	EN 573-3, EN 485
	20.0 °C	65.0 - 71.0 GPa Show Material materials with Elastizitätsmodul of 65.0 - 71.0 GPa	O	DIN 1725-1, EN 573-3, EN 573-4	Flat
Härte, Brinell		45.0 [-] Show Material materials with Härte, Brinell of 45.0 [-]	O	EN 573-3, EN 485
	20.0 °C	45.0 [-] Show Material materials with Härte, Brinell of 45.0 [-]	O	DIN 1725-1, EN 573-3, EN 573-4	Flat
Plane-Strain Fracture Toughnes		22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m				Typical for Wrought 3000 Series Aluminium
Poissonzahl		0.33 [-] Show Material materials with Poissonzahl of 0.33 [-]				Typical for Wrought 3000 Series Aluminium
Schubmodule	20.0 °C	25.0 - 27.0 GPa Show Material materials with Schubmodule of 25.0 - 27.0 GPa	O	DIN 1725-1, EN 573-3, EN 573-4	Flat
Zugfestigkeit	-196.0 °C	290.0 MPa Show Material materials with Zugfestigkeit of 290.0 MPa	O	DIN 1725-1, EN 573-3, EN 573-4
	-80.0 °C	190.0 MPa Show Material materials with Zugfestigkeit of 190.0 MPa	O	DIN 1725-1, EN 573-3, EN 573-4
	-28.0 °C	180.0 MPa Show Material materials with Zugfestigkeit of 180.0 MPa	O	DIN 1725-1, EN 573-3, EN 573-4
	20.0 °C	155.0 - 200.0 MPa Show Material materials with Zugfestigkeit of 155.0 - 200.0 MPa	O	EN 573-3, EN 485, DIN 1725-1, EN 573-4	Flat
	20.0 °C	180.0 MPa Show Material materials with Zugfestigkeit of 180.0 MPa	O	DIN 1725-1, EN 573-3, EN 573-4
	100.0 °C	180.0 MPa Show Material materials with Zugfestigkeit of 180.0 MPa	O	DIN 1725-1, EN 573-3, EN 573-4
	150.0 °C	150.0 MPa Show Material materials with Zugfestigkeit of 150.0 MPa	O	DIN 1725-1, EN 573-3, EN 573-4
	200.0 °C	95.0 MPa Show Material materials with Zugfestigkeit of 95.0 MPa	O	DIN 1725-1, EN 573-3, EN 573-4
	260.0 °C	70.0 MPa Show Material materials with Zugfestigkeit of 70.0 MPa	O	DIN 1725-1, EN 573-3, EN 573-4
	315.0 °C	50.0 MPa Show Material materials with Zugfestigkeit of 50.0 MPa	O	DIN 1725-1, EN 573-3, EN 573-4
	370.0 °C	35.0 MPa Show Material materials with Zugfestigkeit of 35.0 MPa	O	DIN 1725-1, EN 573-3, EN 573-4

Thermisch

Property	Temperature	Value	Condition	Related Standards	Shape
Koeffizient der thermischen Ausdehnung	-50 °C	2.1499999999999997e-05 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 2.1499999999999997e-05 1/K	O	EN 573-3, EN 485
	-50.0 °C	2.15e-05 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 2.15e-05 1/K	O	DIN 1725-1, EN 573-3, EN 573-4	Flat
	20 °C	2.1499999999999997e-05 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 2.1499999999999997e-05 1/K	O	EN 573-3, EN 485
	20 °C	2.3199999999999998e-05 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 2.3199999999999998e-05 1/K	O	EN 573-3, EN 485
	20 °C	2.3899999999999998e-05 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 2.3899999999999998e-05 1/K	O	EN 573-3, EN 485
	20 °C	2.41e-05 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 2.41e-05 1/K	O	EN 573-3, EN 485, DIN 1725-1, EN 573-4	Flat
	20 °C	2.51e-05 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 2.51e-05 1/K	O	EN 573-3, EN 485, DIN 1725-1, EN 573-4	Flat
	100 °C	2.3199999999999998e-05 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 2.3199999999999998e-05 1/K	O	EN 573-3, EN 485
	100.0 °C	2.32e-05 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 2.32e-05 1/K	O	DIN 1725-1, EN 573-3, EN 573-4	Flat
	100 °C	2.3899999999999998e-05 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 2.3899999999999998e-05 1/K	O	EN 573-3, EN 485
	200 °C	2.41e-05 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 2.41e-05 1/K	O	EN 573-3, EN 485, DIN 1725-1, EN 573-4	Flat
	200.0 °C	2.41e-05 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 2.41e-05 1/K	O	EN 573-3, EN 485, DIN 1725-1, EN 573-4	Flat
	300 °C	2.51e-05 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 2.51e-05 1/K	O	EN 573-3, EN 485, DIN 1725-1, EN 573-4	Flat
	300.0 °C	2.51e-05 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 2.51e-05 1/K	O	EN 573-3, EN 485, DIN 1725-1, EN 573-4	Flat
Schmelzpunkt		629.0 - 654.0 °C Show Material materials with Schmelzpunkt of 629.0 - 654.0 °C	O	EN 573-3, EN 485
		630.0 - 655.0 °C Show Material materials with Schmelzpunkt of 630.0 - 655.0 °C	O	EN 573-3, EN 485
Spezifische Wärmekapazität		893.0 J/(kg·K) Show Material materials with Spezifische Wärmekapazität of 893.0 J/(kg·K)	O	EN 573-3, EN 485
	20.0 °C	893.0 J/(kg·K) Show Material materials with Spezifische Wärmekapazität of 893.0 J/(kg·K)	O	DIN 1725-1, EN 573-3, EN 573-4	Flat
Wärmeleitfähigkeit		160.0 - 180.0 W/(m·K) Show Material materials with Wärmeleitfähigkeit of 160.0 - 180.0 W/(m·K)	O	EN 573-3, EN 485
		163 W/(m·K) Show Material materials with Wärmeleitfähigkeit of 163 W/(m·K)	O	EN 573-3, EN 485
	20.0 °C	160.0 - 190.0 W/(m·K) Show Material materials with Wärmeleitfähigkeit of 160.0 - 190.0 W/(m·K)	O	DIN 1725-1, EN 573-3, EN 573-4	Flat

Elektrisch

Property	Temperature	Value	Condition	Related Standards	Shape
Elektrische Leitfähigkeit		23000000.0 - 25000000.0 S/m Show Material materials with Elektrische Leitfähigkeit of 23000000.0 - 25000000.0 S/m	O	EN 573-3, EN 485
		24000000.0 S/m Show Material materials with Elektrische Leitfähigkeit of 24000000.0 S/m	O	EN 573-3, EN 485
	20.0 °C	20000000.0 - 24000000.0 S/m Show Material materials with Elektrische Leitfähigkeit of 20000000.0 - 24000000.0 S/m	O	DIN 1725-1, EN 573-3, EN 573-4	Flat
spezifischer Widerstand		4e-08 - 4.35e-08 Ω·m Show Material materials with spezifischer Widerstand of 4e-08 - 4.35e-08 Ω·m	O	EN 573-3, EN 485
		4.17e-08 Ω·m Show Material materials with spezifischer Widerstand of 4.17e-08 Ω·m	O	EN 573-3, EN 485

Chemical properties

Property	Value	Condition	Related Standards	Shape
Eisen	0.7 % Show Material materials with Eisen of 0.7 %	O	DIN 1725-1, EN 573-3, EN 573-4	Flat
	0.70 % Show Material materials with Eisen of 0.70 %	O	EN 573-3, EN 485
Kupfer	0.25 % Show Material materials with Kupfer of 0.25 %	O	DIN 1725-1, EN 573-3, EN 573-4, EN 485	Flat
Magnesium	0.8 - 1.3 % Show Material materials with Magnesium of 0.8 - 1.3 %	O	DIN 1725-1, EN 573-3, EN 573-4, EN 485	Flat
Mangan	1.0 - 1.5 % Show Material materials with Mangan of 1.0 - 1.5 %	O	DIN 1725-1, EN 573-3, EN 573-4, EN 485	Flat
Silizium	0.3 % Show Material materials with Silizium of 0.3 %	O	DIN 1725-1, EN 573-3, EN 573-4, EN 485	Flat
Zink	0.25 % Show Material materials with Zink of 0.25 %	O	DIN 1725-1, EN 573-3, EN 573-4, EN 485	Flat

Technological properties

Property

Anodizing

decorative: sufficient, Protective: very good

Corrosion properties

Seawater: very good, weathering: very good

Workability

Bending / Spinning (cold): very good / acceptable, Impact extrusion (cold): acceptable, Deep drawing / upsetting (Condition) very good (H14) / acceptable (H12)