Allgemein
Property | Value | Condition | Related Standards |
---|---|---|---|
Dichte | 2.66 g/cm³ Show Material materials with Dichte of 2.66 g/cm³ | H112 | EN 573-3, EN 485, EN 586, EN 603, EN 755 |
Mechanisch
Property | Value | Condition | Related Standards | Comment |
---|---|---|---|---|
Elastizitätsmodul | 70.5 GPa Show Material materials with Elastizitätsmodul of 70.5 GPa | H112 | EN 573-3, EN 485, EN 586, EN 603, EN 755 | |
Härte, Brinell | 50.0 [-] Show Material materials with Härte, Brinell of 50.0 [-] | H112 | EN 573-3, EN 586 | |
52.0 [-] Show Material materials with Härte, Brinell of 52.0 [-] | H112 | EN 573-3, EN 485 | ||
58.0 [-] Show Material materials with Härte, Brinell of 58.0 [-] | H112 | EN 573-3, EN 485 | ||
62.0 [-] Show Material materials with Härte, Brinell of 62.0 [-] | H112 | EN 573-3, EN 485 | ||
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 5000 Series Aluminium | ||
Poissonzahl | 0.33 [-] Show Material materials with Poissonzahl of 0.33 [-] | Typical for Wrought 5000 Series Aluminium | ||
Schubmodule | 26.5 GPa Show Material materials with Schubmodule of 26.5 GPa | H112 | EN 573-3, EN 485, EN 586, EN 603, EN 755 | |
Zugfestigkeit | 180.0 MPa Show Material materials with Zugfestigkeit of 180.0 MPa | H112 | EN 573-3, EN 586, EN 603, EN 755 | |
190.0 MPa Show Material materials with Zugfestigkeit of 190.0 MPa | H112 | EN 573-3, EN 485 |
Thermisch
Property | Temperature | Value | Condition | Related Standards | Comment |
---|---|---|---|---|---|
Koeffizient der thermischen Ausdehnung | 20 °C | 2.3899999999999998e-05 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 2.3899999999999998e-05 1/K | H112 | EN 573-3, EN 485, EN 586, EN 603, EN 755 | |
100 °C | 2.3899999999999998e-05 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 2.3899999999999998e-05 1/K | H112 | EN 573-3, EN 485, EN 586, EN 603, EN 755 | ||
Max. Betriebstemperatur | 150.0 °C Show Material materials with Max. Betriebstemperatur of 150.0 °C | Typical for Wrought 5000 Series Aluminium | |||
Schmelzpunkt | 610.0 - 640.0 °C Show Material materials with Schmelzpunkt of 610.0 - 640.0 °C | H112 | EN 573-3, EN 485, EN 586, EN 603, EN 755 | ||
Spezifische Wärmekapazität | 879.0 - 963.0 J/(kg·K) Show Material materials with Spezifische Wärmekapazität of 879.0 - 963.0 J/(kg·K) | Typical for Wrought 5000 Series Aluminium | |||
Wärmeleitfähigkeit | 140.0 - 160.0 W/(m·K) Show Material materials with Wärmeleitfähigkeit of 140.0 - 160.0 W/(m·K) | H112 | EN 573-3, EN 485, EN 586, EN 603, EN 755 |
Elektrisch
Property | Value | Condition | Related Standards |
---|---|---|---|
Elektrische Leitfähigkeit | 20000000.0 - 23000000.0 S/m Show Material materials with Elektrische Leitfähigkeit of 20000000.0 - 23000000.0 S/m | H112 | EN 573-3, EN 485, EN 586, EN 603, EN 755 |
spezifischer Widerstand | 4.35e-08 - 5e-08 Ω·m Show Material materials with spezifischer Widerstand of 4.35e-08 - 5e-08 Ω·m | H112 | EN 573-3, EN 485, EN 586, EN 603, EN 755 |
Chemical properties
Property | Value | Condition | Related Standards |
---|---|---|---|
Eisen | 0.40 % Show Material materials with Eisen of 0.40 % | H112 | EN 573-3, EN 485, EN 586, EN 603, EN 755 |
Kupfer | 0.1 % Show Material materials with Kupfer of 0.1 % | H112 | EN 573-3, EN 485, EN 586, EN 603, EN 755 |
Magnesium | 2.6 - 3.6 % Show Material materials with Magnesium of 2.6 - 3.6 % | H112 | EN 573-3, EN 485, EN 586, EN 603, EN 755 |
Mangan | 0.5 % Show Material materials with Mangan of 0.5 % | H112 | EN 573-3, EN 485, EN 586, EN 603, EN 755 |
Silizium | 0.4 % Show Material materials with Silizium of 0.4 % | H112 | EN 573-3, EN 485, EN 586, EN 603, EN 755 |
Titan | 0.15 % Show Material materials with Titan of 0.15 % | H112 | EN 573-3, EN 485, EN 586, EN 603, EN 755 |
Zink | 0.2 % Show Material materials with Zink of 0.2 % | H112 | EN 573-3, EN 485, EN 586, EN 603, EN 755 |
Technological properties
Property | ||
---|---|---|
Anodizing | decorative: gut (EQ: sehr gut), Protective: very good | |
Brazing | hard brazing (with flux/ without flux): poor / sufficient, friction soldering: acceptable, soft brazing with flux: poor | |
Corrosion properties | Seawater: very good to good, weathering: very good | |
Workability | Bending / Spinning (cold): good / acceptable, Impact extrusion (cold): sufficient, Deep drawing / upsetting (Condition) good (O) / good (H12) |