Eigenschaften
Allgemein
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Dichte | 2.705 g/cm³ Show Material materials with Dichte of 2.705 g/cm³ | H12 | AA Standards, ASTM B209, ASTM B210, ASTM B483 |
Mechanisch
| Property | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|
Bending Fatigue Strength | 30.0 MPa Show Material materials with Bending Fatigue Strength of 30.0 MPa | H12 | AA Standards | |
Elastizitätsmodul | 69.0 GPa Show Material materials with Elastizitätsmodul of 69.0 GPa | H12 | AA Standards, ASTM B209, ASTM B210, ASTM B483 | |
Härte, Brinell | 23.0 [-] Show Material materials with Härte, Brinell of 23.0 [-] | H12 | AA Standards | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 1000 Series Aluminium | ||
Poissonzahl | 0.33 [-] Show Material materials with Poissonzahl of 0.33 [-] | Typical for Wrought 1000 Series Aluminium | ||
Schubmodule | 25.9 GPa Show Material materials with Schubmodule of 25.9 GPa | Typical for Wrought 1000 Series Aluminium | ||
Zugfestigkeit | 70.0 MPa Show Material materials with Zugfestigkeit of 70.0 MPa | H12 | AA Standards, ASTM B210, ASTM B483 | |
75.0 - 110.0 MPa Show Material materials with Zugfestigkeit of 75.0 - 110.0 MPa | H12 | AA Standards, ASTM B209 | ||
85.0 MPa Show Material materials with Zugfestigkeit of 85.0 MPa | H12 | AA Standards |
Thermisch
| Property | Temperature | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|---|
Koeffizient der thermischen Ausdehnung | 20 °C | 2.36e-05 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 2.36e-05 1/K | H12 | AA Standards, ASTM B209, ASTM B210, ASTM B483 | |
100 °C | 2.36e-05 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 2.36e-05 1/K | H12 | AA Standards, ASTM B209, ASTM B210, ASTM B483 | ||
Schmelzpunkt | 645.0 - 655.0 °C Show Material materials with Schmelzpunkt of 645.0 - 655.0 °C | H12 | AA Standards, ASTM B209, ASTM B210, ASTM B483 | ||
Spezifische Wärmekapazität | 900.0 - 963.0 J/(kg·K) Show Material materials with Spezifische Wärmekapazität of 900.0 - 963.0 J/(kg·K) | Typical for Wrought 1000 Series Aluminium | |||
Wärmeleitfähigkeit | 230.0 - 234.0 W/(m·K) Show Material materials with Wärmeleitfähigkeit of 230.0 - 234.0 W/(m·K) | H12 | AA Standards, ASTM B209, ASTM B210, ASTM B483 |
Elektrisch
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Elektrische Leitfähigkeit | 35000000.0 - 36000000.0 S/m Show Material materials with Elektrische Leitfähigkeit of 35000000.0 - 36000000.0 S/m | H12 | AA Standards, ASTM B209, ASTM B210, ASTM B483 |
spezifischer Widerstand | 2.78e-08 - 2.86e-08 Ω·m Show Material materials with spezifischer Widerstand of 2.78e-08 - 2.86e-08 Ω·m | H12 | AA Standards, ASTM B209, ASTM B210, ASTM B483 |
Chemical properties
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Aluminium | 99.6 % Show Material materials with Aluminium of 99.6 % | H12 | AA Standards, ASTM B209, ASTM B210, ASTM B483 |
Eisen | 0.35 % Show Material materials with Eisen of 0.35 % | H12 | AA Standards, ASTM B209, ASTM B210, ASTM B483 |
Kupfer | 0.05 % Show Material materials with Kupfer of 0.05 % | H12 | AA Standards, ASTM B209, ASTM B210, ASTM B483 |
Magnesium | 0.03 % Show Material materials with Magnesium of 0.03 % | H12 | AA Standards, ASTM B209, ASTM B210, ASTM B483 |
Mangan | 0.03 % Show Material materials with Mangan of 0.03 % | H12 | AA Standards, ASTM B209, ASTM B210, ASTM B483 |
Silizium | 0.25 % Show Material materials with Silizium of 0.25 % | H12 | AA Standards, ASTM B209, ASTM B210, ASTM B483 |
Titan | 0.03 % Show Material materials with Titan of 0.03 % | H12 | AA Standards, ASTM B209, ASTM B210, ASTM B483 |
Vanadium | 0.05 % Show Material materials with Vanadium of 0.05 % | H12 | AA Standards, ASTM B209, ASTM B210, ASTM B483 |
Zink | 0.05 % Show Material materials with Zink of 0.05 % | H12 | AA Standards, ASTM B209, ASTM B210, ASTM B483 |
Technological properties
| Property | ||
|---|---|---|
| Brazing | general: possible with commercial processes and methods | |
| Corrosion properties | Stress corrosion cracking: no damage during operation and laboratory tests, general: very good, without protection in industrial or seawater atmosphere | |
| General machinability | General: not suitable (O, H12), poor (H14, H16, H18) | |
| Workability | general (condition): good (O, H12, H14), acceptable (H16, H18) | |