EN 12844 Grade ZP5

Want to keep this datasheet? Save it now in your required format

Description

The material ZP5 with the material number ZP0410 is the preferred alloy for pressure castings. In its property profile, the alloy combines good mechanical properties with good resistance to corrosion, good dimensional accuracy und stability of accurate dimensions as well as with the possibility to galvanically deposit almost all metals on castings of this alloy. With observance of increased purity and of suitable processing circumstances, the material is applicable in extreme climatic conditions. The tensile strength depends on the wall thickness. With the wall thickness of the casting becoming smaller, the strength increases. The casting temperature ought to be about 425 degrees C (450 degrees C maximum) the forming temperature (pressure casting) is to be adjusted to about 180 to 250 degrees C maximum. According to DIN EN 12844, the alternating stress fatigue strength (time strength) is 56 N/mm² with 100 million reversals of stress the creep life (0.5 per cent, 3000 h) is 100 N/mm². The temperature coefficient of the length is 27 µm/m*K.

Related Standards

Equivalent Materials

Diese Materialdaten wurden von WIAM,AluKey zur Verfügung gestellt

Alle Daten beziehen sich auf Raumtemperatur soweit nicht anderweitig spezifiziert. SI Einheiten werden verwendt soweit nicht anderweitig spezifiziert.
Äquivalente Standards sind ähnlich zu einem oder mehreren Standards die der Anbieter angegeben hat. Manche äquivalente Standards können strikter sein oder außerhalb der Bedingungen des ursprünglichen Standards.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

All categories

Eigenschaften

Allgemein

Property	Temperature	Value
Dichte	20.0 °C	6.7 g/cm³ Show Material materials with Dichte of 6.7 g/cm³

Mechanisch

Property	Temperature	Value	Comment
Bending Fatigue Strength	23.0 °C	56 MPa Show Material materials with Bending Fatigue Strength of 56 MPa
Dehnung	20.0 °C	4 % Show Material materials with Dehnung of 4 %
	80.0 °C	12 % Show Material materials with Dehnung of 12 %
	150.0 °C	25 % Show Material materials with Dehnung of 25 %

Dehnung A50	20.0 °C	5 % Show Material materials with Dehnung A50 of 5 %
	23.0 °C	5 % Show Material materials with Dehnung A50 of 5 %
	Unlock all property charts
Elastizitätsmodul	20.0 °C	85 GPa Show Material materials with Elastizitätsmodul of 85 GPa
Härte, Brinell	20.0 °C	90 - 92 [-] Show Material materials with Härte, Brinell of 90 - 92 [-]
	23.0 °C	92 [-] Show Material materials with Härte, Brinell of 92 [-]
	80.0 °C	65 [-] Show Material materials with Härte, Brinell of 65 [-]
	150.0 °C	38 [-] Show Material materials with Härte, Brinell of 38 [-]
	Unlock all property charts
Poissonzahl	23.0 °C	0.3 [-] Show Material materials with Poissonzahl of 0.3 [-]	Typical for Zinc Aluminium
Streckgrenze Rp 0,2	20.0 °C	230 - 250 MPa Show Material materials with Streckgrenze Rp 0,2 of 230 - 250 MPa
	23.0 °C	250 MPa Show Material materials with Streckgrenze Rp 0,2 of 250 MPa
	80.0 °C	180 MPa Show Material materials with Streckgrenze Rp 0,2 of 180 MPa
	150.0 °C	90 MPa Show Material materials with Streckgrenze Rp 0,2 of 90 MPa
	Unlock all property charts
Zugfestigkeit	20.0 °C	300 - 330 MPa Show Material materials with Zugfestigkeit of 300 - 330 MPa
	23.0 °C	330 MPa Show Material materials with Zugfestigkeit of 330 MPa
	80.0 °C	240 MPa Show Material materials with Zugfestigkeit of 240 MPa
	150.0 °C	160 MPa Show Material materials with Zugfestigkeit of 160 MPa
	Unlock all property charts

Thermisch

Property	Temperature	Value	Comment
Koeffizient der thermischen Ausdehnung	23.0 °C	2.2E-5 - 2.8E-5 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 2.2E-5 - 2.8E-5 1/K	Typical for Zinc Aluminium
Schmelzpunkt		375 - 485 °C Show Material materials with Schmelzpunkt of 375 - 485 °C	Typical for Zinc Aluminium
Spezifische Wärmekapazität	23.0 °C	393 - 525 J/(kg·K) Show Material materials with Spezifische Wärmekapazität of 393 - 525 J/(kg·K)	Typical for Zinc Aluminium
Wärmeleitfähigkeit	20.0 °C	110 W/(m·K) Show Material materials with Wärmeleitfähigkeit of 110 W/(m·K)

Elektrisch

Property	Temperature	Value
Elektrische Leitfähigkeit	20.0 °C	1.51E+7 S/m Show Material materials with Elektrische Leitfähigkeit of 1.51E+7 S/m
spezifischer Widerstand	20.0 °C	6.6E-8 Ω·m Show Material materials with spezifischer Widerstand of 6.6E-8 Ω·m

Chemical properties

Property	Value
Aluminium	3.7 - 4.3 % Show Material materials with Aluminium of 3.7 - 4.3 %
Andere	Rest Zn
Blei	5E-3 % Show Material materials with Blei of 5E-3 %
Cadmium	5E-3 % Show Material materials with Cadmium of 5E-3 %
Eisen	0.05 % Show Material materials with Eisen of 0.05 %
Kupfer	0.7 - 1.2 % Show Material materials with Kupfer of 0.7 - 1.2 %
Magnesium	0.03 - 0.06 % Show Material materials with Magnesium of 0.03 - 0.06 %
Nickel	0.02 % Show Material materials with Nickel of 0.02 %
Silizium	0.03 % Show Material materials with Silizium of 0.03 %
Zink	94.33 % Show Material materials with Zink of 94.33 %
Zinn	2E-3 % Show Material materials with Zinn of 2E-3 %

Looking for suppliers of this material? Click to see 1 supplier of EN 12844 Grade ZP5 on Matmatch