Eigenschaften
Allgemein
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Dichte | 2.72 g/cmÂł Show Material materials with Dichte of 2.72 g/cmÂł | H38 | AA Standards, ASTM B209, ASTM B313 |
Mechanisch
| Property | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|
Bending Fatigue Strength | 110.0 MPa Show Material materials with Bending Fatigue Strength of 110.0 MPa | H38 | AA Standards | |
ElastizitÀtsmodul | 69.0 GPa Show Material materials with ElastizitÀtsmodul of 69.0 GPa | H38 | AA Standards, ASTM B209, ASTM B313 | |
HĂ€rte, Brinell | 77.0 [-] Show Material materials with HĂ€rte, Brinell of 77.0 [-] | H38 | AA Standards | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·âm Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·âm | Typical for Wrought 3000 Series Aluminium | ||
Poissonzahl | 0.33 [-] Show Material materials with Poissonzahl of 0.33 [-] | Typical for Wrought 3000 Series Aluminium | ||
Schubmodule | 25.0 - 26.0 GPa Show Material materials with Schubmodule of 25.0 - 26.0 GPa | Typical for Wrought 3000 Series Aluminium | ||
Zugfestigkeit | 260.0 MPa Show Material materials with Zugfestigkeit of 260.0 MPa | H38 | AA Standards, ASTM B209, ASTM B313 | |
285.0 MPa Show Material materials with Zugfestigkeit of 285.0 MPa | H38 | AA Standards |
Thermisch
| Property | Temperature | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|---|
Koeffizient der thermischen Ausdehnung | 20 °C | 2.3899999999999998e-05 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 2.3899999999999998e-05 1/K | H38 | AA Standards, ASTM B209, ASTM B313 | |
100 °C | 2.3899999999999998e-05 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 2.3899999999999998e-05 1/K | H38 | AA Standards, ASTM B209, ASTM B313 | ||
Schmelzpunkt | 630.0 - 655.0 °C Show Material materials with Schmelzpunkt of 630.0 - 655.0 °C | H38 | AA Standards, ASTM B209, ASTM B313 | ||
Spezifische WÀrmekapazitÀt | 893.0 - 920.0 J/(kg·K) Show Material materials with Spezifische WÀrmekapazitÀt of 893.0 - 920.0 J/(kg·K) | Typical for Wrought 3000 Series Aluminium | |||
WÀrmeleitfÀhigkeit | 163 W/(m·K) Show Material materials with WÀrmeleitfÀhigkeit of 163 W/(m·K) | H38 | AA Standards, ASTM B209, ASTM B313 |
Elektrisch
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Elektrische LeitfÀhigkeit | 24000000.0 S/m Show Material materials with Elektrische LeitfÀhigkeit of 24000000.0 S/m | H38 | AA Standards, ASTM B209, ASTM B313 |
spezifischer Widerstand | 4.17e-08 Ω·m Show Material materials with spezifischer Widerstand of 4.17e-08 Ω·m | H38 | AA Standards, ASTM B209, ASTM B313 |
Chemical properties
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Eisen | 0.70 % Show Material materials with Eisen of 0.70 % | H38 | AA Standards, ASTM B209, ASTM B313 |
Kupfer | 0.25 % Show Material materials with Kupfer of 0.25 % | H38 | AA Standards, ASTM B209, ASTM B313 |
Magnesium | 0.8 - 1.3 % Show Material materials with Magnesium of 0.8 - 1.3 % | H38 | AA Standards, ASTM B209, ASTM B313 |
Mangan | 1.0 - 1.5 % Show Material materials with Mangan of 1.0 - 1.5 % | H38 | AA Standards, ASTM B209, ASTM B313 |
Silizium | 0.3 % Show Material materials with Silizium of 0.3 % | H38 | AA Standards, ASTM B209, ASTM B313 |
Zink | 0.25 % Show Material materials with Zink of 0.25 % | H38 | AA Standards, ASTM B209, ASTM B313 |
Technological properties
| Property | ||
|---|---|---|
| Brazing | general: Lötbar mit speziellen Techniken oder bei bestimmten Anwendungen | |
| Corrosion properties | Stress corrosion cracking: no damage during operation and laboratory tests, general: very good, without protection in industrial or seawater atmosphere | |
| General machinability | General: poor (O, H32), sufficient (H34, H36, H38) | |
| Workability | general (condition): good (O), acceptable (H32, H34), poor(H36, H38) | |