Eigenschaften
Allgemein
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Dichte | 2.72 g/cm³ Show Material materials with Dichte of 2.72 g/cm³ | O | AA Standards, ASTM B209, ASTM B221, ASTM B313, ASTM B547 |
Mechanisch
| Property | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|
Bending Fatigue Strength | 95.0 MPa Show Material materials with Bending Fatigue Strength of 95.0 MPa | O | AA Standards | |
Elastizitätsmodul | 69.0 GPa Show Material materials with Elastizitätsmodul of 69.0 GPa | O | AA Standards, ASTM B209, ASTM B221, ASTM B313, ASTM B547 | |
Härte, Brinell | 45.0 [-] Show Material materials with Härte, Brinell of 45.0 [-] | O | AA Standards | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 3000 Series Aluminium | ||
Poissonzahl | 0.33 [-] Show Material materials with Poissonzahl of 0.33 [-] | Typical for Wrought 3000 Series Aluminium | ||
Schubmodule | 25.0 - 26.0 GPa Show Material materials with Schubmodule of 25.0 - 26.0 GPa | Typical for Wrought 3000 Series Aluminium | ||
Zugfestigkeit | 150.0 - 200.0 MPa Show Material materials with Zugfestigkeit of 150.0 - 200.0 MPa | O | AA Standards, ASTM B209, ASTM B313, ASTM B547 | |
160.0 - 200.0 MPa Show Material materials with Zugfestigkeit of 160.0 - 200.0 MPa | O | AA Standards, ASTM B221 | ||
180.0 MPa Show Material materials with Zugfestigkeit of 180.0 MPa | O | AA Standards |
Thermisch
| Property | Temperature | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|---|
Koeffizient der thermischen Ausdehnung | 20 °C | 2.3899999999999998e-05 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 2.3899999999999998e-05 1/K | O | AA Standards, ASTM B209, ASTM B221, ASTM B313, ASTM B547 | |
100 °C | 2.3899999999999998e-05 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 2.3899999999999998e-05 1/K | O | AA Standards, ASTM B209, ASTM B221, ASTM B313, ASTM B547 | ||
Schmelzpunkt | 630.0 - 655.0 °C Show Material materials with Schmelzpunkt of 630.0 - 655.0 °C | O | AA Standards, ASTM B209, ASTM B221, ASTM B313, ASTM B547 | ||
Spezifische Wärmekapazität | 893.0 - 920.0 J/(kg·K) Show Material materials with Spezifische Wärmekapazität of 893.0 - 920.0 J/(kg·K) | Typical for Wrought 3000 Series Aluminium | |||
Wärmeleitfähigkeit | 163 W/(m·K) Show Material materials with Wärmeleitfähigkeit of 163 W/(m·K) | O | AA Standards, ASTM B209, ASTM B221, ASTM B313, ASTM B547 |
Elektrisch
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Elektrische Leitfähigkeit | 24000000.0 S/m Show Material materials with Elektrische Leitfähigkeit of 24000000.0 S/m | O | AA Standards, ASTM B209, ASTM B221, ASTM B313, ASTM B547 |
spezifischer Widerstand | 4.17e-08 Ω·m Show Material materials with spezifischer Widerstand of 4.17e-08 Ω·m | O | AA Standards, ASTM B209, ASTM B221, ASTM B313, ASTM B547 |
Chemical properties
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Eisen | 0.70 % Show Material materials with Eisen of 0.70 % | O | AA Standards, ASTM B209, ASTM B221, ASTM B313, ASTM B547 |
Kupfer | 0.25 % Show Material materials with Kupfer of 0.25 % | O | AA Standards, ASTM B209, ASTM B221, ASTM B313, ASTM B547 |
Magnesium | 0.8 - 1.3 % Show Material materials with Magnesium of 0.8 - 1.3 % | O | AA Standards, ASTM B209, ASTM B221, ASTM B313, ASTM B547 |
Mangan | 1.0 - 1.5 % Show Material materials with Mangan of 1.0 - 1.5 % | O | AA Standards, ASTM B209, ASTM B221, ASTM B313, ASTM B547 |
Silizium | 0.3 % Show Material materials with Silizium of 0.3 % | O | AA Standards, ASTM B209, ASTM B221, ASTM B313, ASTM B547 |
Zink | 0.25 % Show Material materials with Zink of 0.25 % | O | AA Standards, ASTM B209, ASTM B221, ASTM B313, ASTM B547 |
Technological properties
| Property | ||
|---|---|---|
| Brazing | general: Lötbar mit speziellen Techniken oder bei bestimmten Anwendungen | |
| Corrosion properties | Stress corrosion cracking: no damage during operation and laboratory tests, general: very good, without protection in industrial or seawater atmosphere | |
| General machinability | General: poor (O, H32), sufficient (H34, H36, H38) | |
| Workability | general (condition): good (O), acceptable (H32, H34), poor(H36, H38) | |