Allgemein
Property | Value | Condition | Related Standards |
---|---|---|---|
Dichte | 2.7 g/cm³ Show Material materials with Dichte of 2.7 g/cm³ | O | AA Standards, ASTM B209, ASTM B210, ASTM B316, ASTM B483 |
Mechanisch
Property | Value | Condition | Related Standards | Comment |
---|---|---|---|---|
Elastizitätsmodul | 69.0 GPa Show Material materials with Elastizitätsmodul of 69.0 GPa | O | AA Standards, ASTM B209, ASTM B210, ASTM B316, ASTM B483 | |
Härte, Brinell | 28.0 [-] Show Material materials with Härte, Brinell of 28.0 [-] | O | AA Standards | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 5000 Series Aluminium | ||
Poissonzahl | 0.33 [-] Show Material materials with Poissonzahl of 0.33 [-] | Typical for Wrought 5000 Series Aluminium | ||
Schubmodule | 26.0 - 26.5 GPa Show Material materials with Schubmodule of 26.0 - 26.5 GPa | Typical for Wrought 5000 Series Aluminium | ||
Zugfestigkeit | 105.0 - 145.0 MPa Show Material materials with Zugfestigkeit of 105.0 - 145.0 MPa | O | AA Standards, ASTM B209, ASTM B210 | |
105.0 MPa Show Material materials with Zugfestigkeit of 105.0 MPa | O | AA Standards, ASTM B483 | ||
125.0 MPa Show Material materials with Zugfestigkeit of 125.0 MPa | O | AA Standards | ||
140.0 MPa Show Material materials with Zugfestigkeit of 140.0 MPa | O | AA Standards, ASTM B316 |
Thermisch
Property | Temperature | Value | Condition | Related Standards | Comment |
---|---|---|---|---|---|
Koeffizient der thermischen Ausdehnung | 20 °C | 2.38e-05 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 2.38e-05 1/K | O | AA Standards, ASTM B209, ASTM B210, ASTM B316, ASTM B483 | |
100 °C | 2.38e-05 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 2.38e-05 1/K | O | AA Standards, ASTM B209, ASTM B210, ASTM B316, ASTM B483 | ||
Max. Betriebstemperatur | 150.0 °C Show Material materials with Max. Betriebstemperatur of 150.0 °C | Typical for Wrought 5000 Series Aluminium | |||
Schmelzpunkt | 630.0 - 655.0 °C Show Material materials with Schmelzpunkt of 630.0 - 655.0 °C | O | AA Standards, ASTM B209, ASTM B210, ASTM B316, ASTM B483 | ||
Spezifische Wärmekapazität | 879.0 - 963.0 J/(kg·K) Show Material materials with Spezifische Wärmekapazität of 879.0 - 963.0 J/(kg·K) | Typical for Wrought 5000 Series Aluminium | |||
Wärmeleitfähigkeit | 201 W/(m·K) Show Material materials with Wärmeleitfähigkeit of 201 W/(m·K) | O | AA Standards, ASTM B209, ASTM B210, ASTM B316, ASTM B483 |
Elektrisch
Property | Value | Condition | Related Standards |
---|---|---|---|
Elektrische Leitfähigkeit | 30000000.0 S/m Show Material materials with Elektrische Leitfähigkeit of 30000000.0 S/m | O | AA Standards, ASTM B209, ASTM B210, ASTM B316, ASTM B483 |
spezifischer Widerstand | 3.33e-08 Ω·m Show Material materials with spezifischer Widerstand of 3.33e-08 Ω·m | O | AA Standards, ASTM B209, ASTM B210, ASTM B316, ASTM B483 |
Chemical properties
Property | Value | Condition | Related Standards |
---|---|---|---|
Chrom | 0.1 % Show Material materials with Chrom of 0.1 % | O | AA Standards, ASTM B209, ASTM B210, ASTM B316, ASTM B483 |
Eisen | 0.70 % Show Material materials with Eisen of 0.70 % | O | AA Standards, ASTM B209, ASTM B210, ASTM B316, ASTM B483 |
Kupfer | 0.2 % Show Material materials with Kupfer of 0.2 % | O | AA Standards, ASTM B209, ASTM B210, ASTM B316, ASTM B483 |
Magnesium | 0.5 - 1.1 % Show Material materials with Magnesium of 0.5 - 1.1 % | O | AA Standards, ASTM B209, ASTM B210, ASTM B316, ASTM B483 |
Mangan | 0.2 % Show Material materials with Mangan of 0.2 % | O | AA Standards, ASTM B209, ASTM B210, ASTM B316, ASTM B483 |
Silizium | 0.3 % Show Material materials with Silizium of 0.3 % | O | AA Standards, ASTM B209, ASTM B210, ASTM B316, ASTM B483 |
Zink | 0.25 % Show Material materials with Zink of 0.25 % | O | AA Standards, ASTM B209, ASTM B210, ASTM B316, ASTM B483 |
Technological properties
Property | ||
---|---|---|
Brazing | general: Lötbar mit speziellen Techniken oder bei bestimmten Anwendungen | |
Corrosion properties | Stress corrosion cracking: no damage during operation and laboratory tests, general: very good, without protection in industrial or seawater atmosphere | |
General machinability | General: not suitable (O, H12, H32), poor (H14, H34, H16, H18, H36, H38) | |
Workability | general (condition): good (O, H12, H32), acceptable (H14, H34), poor(H16, H18, H36, H38) |