Property | Value | Comment |
---|---|---|
Carbon equivalent (CEV) | 0.15 [-] Show Supplier Material materials with Carbon equivalent (CEV) of 0.15 [-] | max. |
Abmessung
Property | Value |
---|---|
Dimensions | Please feel free to check the figure on the right side of the material page for more details. |
Mechanisch
Property | Value | Comment |
---|---|---|
Dehnung | 32 % Show Supplier Material materials with Dehnung of 32 % | min. | for thickness 1.8-2 mm | Transverse, A80 |
32 % Show Supplier Material materials with Dehnung of 32 % | min. | for thickness 2-3 mm | Transverse, A80 | |
37 % Show Supplier Material materials with Dehnung of 37 % | min. A5.65√So | for thickness 3-13 mm | |
Streckgrenze | 200 - 310 MPa Show Supplier Material materials with Streckgrenze of 200 - 310 MPa | for thickness 1.8-2 mm | Transverse |
200 - 290 MPa Show Supplier Material materials with Streckgrenze of 200 - 290 MPa | for thickness 2-6 mm | Transverse | |
Zugfestigkeit | 300 - 380 MPa Show Supplier Material materials with Zugfestigkeit of 300 - 380 MPa | for thickness 1.8-13 mm | Transverse |
Chemical properties
Property | Value | Comment |
---|---|---|
Aluminium | 0.02 % Show Supplier Material materials with Aluminium of 0.02 % | min. |
Bor | 0.002 - 0.005 % Show Supplier Material materials with Bor of 0.002 - 0.005 % | |
Kohlenstoff | 0.02 - 0.08 % Show Supplier Material materials with Kohlenstoff of 0.02 - 0.08 % | |
Mangan | 0.35 % Show Supplier Material materials with Mangan of 0.35 % | max. |
Phosphor | 0.025 % Show Supplier Material materials with Phosphor of 0.025 % | max. |
Schwefel | 0.02 % Show Supplier Material materials with Schwefel of 0.02 % | max. |
Silizium | 0.03 % Show Supplier Material materials with Silizium of 0.03 % | max. |
Technological properties
Property | ||
---|---|---|
Application areas | Structural forming grade which is well suited to applications requiring high reproducibility of processing performance (especially control of springback). That is why the S200D AM FCE grade is especially suitable for applications such as compressor casings. | |
Chemical composition | The chemical properties given are based on cast analysis data. | |
Coating | Galvanisation: Class 1 |