Property | Value | Comment |
---|---|---|
Carbon equivalent (CEV) | 0.18 [-] Show Supplier Material materials with Carbon equivalent (CEV) of 0.18 [-] | max. |
Abmessung
Property | Value |
---|---|
Dimensions | *Pickled products with thicknesses up to 15 mm may be delivered after prior agreement: please contact us. Please feel free to check the figure on the right side of the material page for more details. |
Mechanisch
Property | Temperature | Value | Comment |
---|---|---|---|
Dehnung | 26 % Show Supplier Material materials with Dehnung of 26 % | min. | for thickness < 3 mm | Transverse, A80 | |
27 % Show Supplier Material materials with Dehnung of 27 % | min. | for thickness < 3 mm, A80 | ||
31 % Show Supplier Material materials with Dehnung of 31 % | min. A5.65√So | for thickness 3-16 mm | Transverse | ||
32 % Show Supplier Material materials with Dehnung of 32 % | min. A5.65√So | for thickness 3-16 mm | ||
Kerbschlagenergie | -20 °C | 40 J Show Supplier Material materials with Kerbschlagenergie of 40 J | min. | for thickness 6-16 mm |
Streckgrenze | 240 - 320 MPa Show Supplier Material materials with Streckgrenze of 240 - 320 MPa | for thickness < 16 mm | |
260 - 340 MPa Show Supplier Material materials with Streckgrenze of 260 - 340 MPa | for thickness < 16 mm | Transverse | ||
Zugfestigkeit | 340 - 450 MPa Show Supplier Material materials with Zugfestigkeit of 340 - 450 MPa | for thickness < 16 mm | Transverse/Longitudinal |
Chemical properties
Property | Value | Comment |
---|---|---|
Aluminium | 0.015 % Show Supplier Material materials with Aluminium of 0.015 % | min. |
Kohlenstoff | 0.1 % Show Supplier Material materials with Kohlenstoff of 0.1 % | max. |
Mangan | 0.8 % Show Supplier Material materials with Mangan of 0.8 % | max. |
Niobium | 0.025 % Show Supplier Material materials with Niobium of 0.025 % | max. |
Phosphor | 0.02 % Show Supplier Material materials with Phosphor of 0.02 % | max. |
Schwefel | 0.02 % Show Supplier Material materials with Schwefel of 0.02 % | max. |
Silizium | 0.03 % Show Supplier Material materials with Silizium of 0.03 % | max. |
Titan | 0.15 % Show Supplier Material materials with Titan of 0.15 % | max. |
Vanadium | 0.2 % Show Supplier Material materials with Vanadium of 0.2 % | max. |
Technological properties
Property | ||
---|---|---|
Application areas | High strength Amstrong® steels are used in a wide range of applications in transport (earth movers, trailers, agricultural and railroad machinery etc), profiling (racks etc) and building (cranes, safety barriers, light poles etc). Significant weight reductions can be achieved by using Amstrong® steels, especially for cranes and heavy vehicle trailers, thus allowing a larger payload. | |
Chemical composition | The chemical properties given are based on cast analysis data. | |
Coating | Galvanisation: Class 1 Suitability for hot-dip zinc coating is defined as per the requirements of EN ISO 14713-2 Table 1 and NFA 35-503. | |
Other | Toughness guarantee at -40°C: on request |