Allgemein
Property | Value | Comment |
---|---|---|
Carbon equivalent (CEV) | 0.32 [-] Show Supplier Material materials with Carbon equivalent (CEV) of 0.32 [-] | max. |
Abmessung
Property | Value |
---|---|
Dimensions | *Pickled products with thicknesses up to 15 mm may be delivered after prior agreement: please contact us. Please feel free to check the figure on the right side of the material page for more details. |
Mechanisch
Property | Temperature | Value | Comment |
---|---|---|---|
Dehnung | 21 % Show Supplier Material materials with Dehnung of 21 % | min. | for thickness < 3 mm | Transverse, A80 | |
22 % Show Supplier Material materials with Dehnung of 22 % | min. | for thickness < 3 mm, A80 | ||
24 % Show Supplier Material materials with Dehnung of 24 % | min. A5.65√So | for thickness 3-16 mm | Transverse | ||
25 % Show Supplier Material materials with Dehnung of 25 % | min. A5.65√So | for thickness 3-16 mm | ||
Kerbschlagenergie | -20 °C | 40 J Show Supplier Material materials with Kerbschlagenergie of 40 J | min. | for thickness 6-16 mm |
Streckgrenze | 355 - 435 MPa Show Supplier Material materials with Streckgrenze of 355 - 435 MPa | for thickness < 16 mm | |
380 - 460 MPa Show Supplier Material materials with Streckgrenze of 380 - 460 MPa | for thickness < 16 mm | Transverse | ||
Zugfestigkeit | 430 - 520 MPa Show Supplier Material materials with Zugfestigkeit of 430 - 520 MPa | for thickness < 16 mm | |
440 - 530 MPa Show Supplier Material materials with Zugfestigkeit of 440 - 530 MPa | for thickness < 16 mm | Transverse |
Chemical properties
Property | Value | Comment |
---|---|---|
Aluminium | 0.015 % Show Supplier Material materials with Aluminium of 0.015 % | min. |
Kohlenstoff | 0.1 % Show Supplier Material materials with Kohlenstoff of 0.1 % | max. |
Mangan | 1.4 % Show Supplier Material materials with Mangan of 1.4 % | max. |
Niobium | 0.065 % Show Supplier Material materials with Niobium of 0.065 % | max. |
Phosphor | 0.02 % Show Supplier Material materials with Phosphor of 0.02 % | max. |
Schwefel | 0.015 % Show Supplier Material materials with Schwefel of 0.015 % | max. |
Silizium | 0.03 % Show Supplier Material materials with Silizium of 0.03 % | max. |
Titan | 0.15 % Show Supplier Material materials with Titan of 0.15 % | max. |
Vanadium | 0.2 % Show Supplier Material materials with Vanadium of 0.2 % | max. |
Technological properties
Property | ||
---|---|---|
Application areas | High strength Amstrong® steels are used in a wide range of applications in transport (earth movers, trailers, agricultural and railroad machinery etc), profiling (racks etc) and building (cranes, safety barriers, light poles etc). Significant weight reductions can be achieved by using Amstrong® steels, especially for cranes and heavy vehicle trailers, thus allowing a larger payload. | |
Chemical composition | The chemical properties given are based on cast analysis data. | |
Coating | Galvanisation: Class 1 Suitability for hot-dip zinc coating is defined as per the requirements of EN ISO 14713-2 Table 1 and NFA 35-503. | |
Other | Toughness guarantee at -40°C: on request |