Eigenschaften
Abmessung
| Property | Value |
|---|---|
Dimensions | For Pickled products, please contact the supplier. Please feel free to check the figure on the right side of the material page for more details. |
Mechanisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dehnung | 18 % Show Supplier Material materials with Dehnung of 18 % | min. | for thickness 1.7-3 mm | Transverse, A80 | |
22 % Show Supplier Material materials with Dehnung of 22 % | min. A5.65√So | for thickness 3-16 mm | Transverse | ||
Kerbschlagenergie | -20 °C | 30 J Show Supplier Material materials with Kerbschlagenergie of 30 J | min. | for thickness 6-16 mm | Transverse |
-20 °C | 45 J Show Supplier Material materials with Kerbschlagenergie of 45 J | min. | for thickness 6-16 mm | |
0 °C | 40 J Show Supplier Material materials with Kerbschlagenergie of 40 J | min. | for thickness 6-16 mm | Transverse | |
0 °C | 65 J Show Supplier Material materials with Kerbschlagenergie of 65 J | min. | for thickness 6-16 mm | |
20 °C | 50 J Show Supplier Material materials with Kerbschlagenergie of 50 J | min. | for thickness 6-16 mm | Transverse | |
20 °C | 75 J Show Supplier Material materials with Kerbschlagenergie of 75 J | min. | for thickness 6-16 mm | |
Streckgrenze | 355 MPa Show Supplier Material materials with Streckgrenze of 355 MPa | min. | for thickness 1.7-16 mm | Transverse | |
Zugfestigkeit | 490 - 630 MPa Show Supplier Material materials with Zugfestigkeit of 490 - 630 MPa | for thickness 1.7-16 mm | Transverse |
Chemical properties
| Property | Value | Comment |
|---|---|---|
Aluminium | 0.02 % Show Supplier Material materials with Aluminium of 0.02 % | min. |
Chrom | 0.3 % Show Supplier Material materials with Chrom of 0.3 % | max. |
Kohlenstoff | 0.18 % Show Supplier Material materials with Kohlenstoff of 0.18 % | max. |
Kupfer | 0.3 % Show Supplier Material materials with Kupfer of 0.3 % | max. |
Mangan | 1.1 - 1.7 % Show Supplier Material materials with Mangan of 1.1 - 1.7 % | |
Molybdän | 0.08 % Show Supplier Material materials with Molybdän of 0.08 % | max. |
Nickel | 0.5 % Show Supplier Material materials with Nickel of 0.5 % | max. |
Niobium | 0.05 % Show Supplier Material materials with Niobium of 0.05 % | max. |
Phosphor | 0.025 % Show Supplier Material materials with Phosphor of 0.025 % | max. |
Schwefel | 0.01 % Show Supplier Material materials with Schwefel of 0.01 % | max. |
Silizium | 0.5 % Show Supplier Material materials with Silizium of 0.5 % | max. |
Stickstoff | 0.012 % Show Supplier Material materials with Stickstoff of 0.012 % | max. |
Titan | 0.03 % Show Supplier Material materials with Titan of 0.03 % | max. |
Vanadium | 0.05 % Show Supplier Material materials with Vanadium of 0.05 % | max. |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Steels for pressure vessels are mainly used to manufacture boilers, drums, pressure or steam piping, industrial thermal vessels and heat exchangers. These steels are suitable for mechanical forming and welding. | |
| Chemical composition | Notes: 1. A ratio Al/N ≥ 2 shall be applied. 2. The sum of the percentages by mass of the three elements chromium, copper and molybdenum shall not exceed 0.45%. 3. The sum of the percentages by mass of the three elements niobium, titanium and vanadium shall not exceed 0.12%. | |
| Other | Mechanical properties: The minimum impact energy values specified apply, even if they are not to be verified in the case of product thicknesses < 6 mm. Where minimum impact energy values are specified for several temperatures, verification of the impact energy, unless otherwise agreed, shall be carried out at the temperature for which the value of 27 J is specified. Where the minimum impact energy value specified at the lowest temperature is higher than 27 J, this higher value shall be verified. | |