Property | Value |
---|---|
Dimensions | Please feel free to check the figure on the right side of the material page for more details. |
Mechanisch
Property | Value | Comment |
---|---|---|
Dehnung | 36 % Show Supplier Material materials with Dehnung of 36 % | min. | for thickness 0.5-0.7 mm | Transverse | A80 |
38 % Show Supplier Material materials with Dehnung of 38 % | min. | for thickness 0.7-2 mm | Transverse | A80 | |
Plastic strain ratio | 1.8 [-] Show Supplier Material materials with Plastic strain ratio of 1.8 [-] | min. | 90ᵒ Transverse | for thickness 0.5-2 mm |
Strain hardening exponent | 0.18 [-] Show Supplier Material materials with Strain hardening exponent of 0.18 [-] | min. | 90ᵒ Transverse | for thickness 0.5-2 mm |
Streckgrenze | 140 - 230 MPa Show Supplier Material materials with Streckgrenze of 140 - 230 MPa | for thickness 0.5-0.7 mm | Transverse |
140 - 210 MPa Show Supplier Material materials with Streckgrenze of 140 - 210 MPa | for thickness 0.7-2 mm | Transverse | |
Zugfestigkeit | 270 - 350 MPa Show Supplier Material materials with Zugfestigkeit of 270 - 350 MPa | for thickness 0.5-2 mm | Transverse |
Chemical properties
Property | Value | Comment |
---|---|---|
Kohlenstoff | 0.08 % Show Supplier Material materials with Kohlenstoff of 0.08 % | max. |
Mangan | 0.4 % Show Supplier Material materials with Mangan of 0.4 % | max. |
Phosphor | 0.03 % Show Supplier Material materials with Phosphor of 0.03 % | max. |
Schwefel | 0.03 % Show Supplier Material materials with Schwefel of 0.03 % | max. |
Silizium | 0.03 % Show Supplier Material materials with Silizium of 0.03 % | max. |
Technological properties
Property | ||
---|---|---|
Application areas | The main areas of use are: Blued steels are suitable for food contact, under certain conditions laid down in European Regulation (EC) No. 1935/2004 and French standard NF A 36-714. Please contact us for further information on this subject. | |
Coating | DC04BS AM FCE can be supplied with or without oil film. | |
Corrosion properties | Corrosion resistance is better than for uncoated cold rolled steels, but is nevertheless limited, particularly in humid atmospheres (salt spray test). | |
Processing methods | The processing conditions for DC04BS AM FCE is similar to those for cold forming. However, in the case of difficult drawing operations, the oxide layer may crack and lose its continuity. |