Allgemein
Property | Value | Comment |
---|---|---|
Dichte | 7.65 g/cm³ Show Supplier Material materials with Dichte of 7.65 g/cm³ | for thickness 0.65 mm |
Mechanisch
Property | Value | Comment |
---|---|---|
Dehnung | 20 - 30 % Show Supplier Material materials with Dehnung of 20 - 30 % | for thickness 0.65 mm | Transverse | A80 |
Härte, Vickers | 200 - 230 [-] Show Supplier Material materials with Härte, Vickers of 200 - 230 [-] | for thickness 0.65 mm |
Number of bends | 2 [-] Show Supplier Material materials with Number of bends of 2 [-] | min. for thickness 0.65 mm | Guaranteed |
Streckgrenze | 370 - 420 MPa Show Supplier Material materials with Streckgrenze of 370 - 420 MPa | for thickness 0.65 mm | Transverse |
Yield to strength ratio | 0.71 - 0.76 [-] Show Supplier Material materials with Yield to strength ratio of 0.71 - 0.76 [-] | for thickness 0.65 mm |
Zugfestigkeit | 520 - 570 MPa Show Supplier Material materials with Zugfestigkeit of 520 - 570 MPa | for thickness 0.65 mm | Transverse |
Magnetisch
Property | Value | Frequency | Comment |
---|---|---|---|
Anisotropy of loss | 14 % Show Supplier Material materials with Anisotropy of loss of 14 % | (+/-) for thickness 0.65 mm | Guaranteed | |
Garantierte Polarisierung | 1.52 [-] Show Supplier Material materials with Garantierte Polarisierung of 1.52 [-] | min. | for thickness 0.65 mm | at 2500 A/m | |
1.62 [-] Show Supplier Material materials with Garantierte Polarisierung of 1.62 [-] | min. | for thickness 0.65 mm | at 5000 A/m | ||
1.72 [-] Show Supplier Material materials with Garantierte Polarisierung of 1.72 [-] | min. | for thickness 0.65 mm | at 10000 A/m | ||
Stacking factor | 0.97 mm Show Supplier Material materials with Stacking factor of 0.97 mm | min. | for thickness 0.65 mm | Guaranteed | |
Typischer Kernverlust | 1.7 W/kg Show Supplier Material materials with Typischer Kernverlust of 1.7 W/kg | 50Hz | max. for thickness 0.65 mm | at 1 T |
5.2 W/kg Show Supplier Material materials with Typischer Kernverlust of 5.2 W/kg | 60Hz | max. for thickness 0.65 mm | at 1.5 T |
Technological properties
Property | ||
---|---|---|
Application areas | The fully processed steel is designed for the manufacture of magnetic circuits for motors, transformers and other electrical equipment. The principal applications are in the electrical engineering, domestic appliance, automotive and building industries. Low loss fully processed steels are also suitable for shielding applications at low frequencies (e.g. housings around electrical systems). | |
Coating | This standard grade is available non-insulated or varnished with any of the coating types described in the following link https://industry.arcelormittal.com/catalogue/D28/EN . | |
Other | Recommendations for use The are obtained without heat treatment after stamping. The material as supplied possesses all the required magnetic properties. |