Allgemein
Property | Value | Comment |
---|---|---|
Dichte | 7.75 g/cm³ Show Supplier Material materials with Dichte of 7.75 g/cm³ | for thickness 0.35 mm |
Mechanisch
Property | Value | Comment |
---|---|---|
Dehnung | 25 - 35 % Show Supplier Material materials with Dehnung of 25 - 35 % | for thickness 0.35 mm | Transverse | A80 |
Härte, Vickers | 130 - 160 [-] Show Supplier Material materials with Härte, Vickers of 130 - 160 [-] | for thickness 0.35 mm |
Number of bends | 3 [-] Show Supplier Material materials with Number of bends of 3 [-] | min. for thickness 0.35 mm | Guaranteed |
Streckgrenze | 250 - 300 MPa Show Supplier Material materials with Streckgrenze of 250 - 300 MPa | for thickness 0.35 mm | Transverse |
Yield to strength ratio | 0.61 - 0.66 [-] Show Supplier Material materials with Yield to strength ratio of 0.61 - 0.66 [-] | for thickness 0.35 mm |
Zugfestigkeit | 415 - 455 MPa Show Supplier Material materials with Zugfestigkeit of 415 - 455 MPa | for thickness 0.35 mm | Transverse |
Magnetisch
Property | Value | Frequency | Comment |
---|---|---|---|
Anisotropy of loss | 17 % Show Supplier Material materials with Anisotropy of loss of 17 % | (+/-) for thickness 0.35 mm | Guaranteed | |
Garantierte Polarisierung | 1.61 [-] Show Supplier Material materials with Garantierte Polarisierung of 1.61 [-] | min. | for thickness 0.35 mm | at 2500 A/m | |
1.7 [-] Show Supplier Material materials with Garantierte Polarisierung of 1.7 [-] | min. | for thickness 0.35 mm | Indicative | ||
1.82 [-] Show Supplier Material materials with Garantierte Polarisierung of 1.82 [-] | min. | for thickness 0.35 mm | at 10000 A/m | ||
Garantierter Kernverlust | 3.3 W/kg Show Supplier Material materials with Garantierter Kernverlust of 3.3 W/kg | 50Hz | max. for thickness 0.35 mm | at 1.5 T |
Stacking factor | 0.95 mm Show Supplier Material materials with Stacking factor of 0.95 mm | min. | for thickness 0.35 mm | Guaranteed | |
Typischer Kernverlust | 1.35 W/kg Show Supplier Material materials with Typischer Kernverlust of 1.35 W/kg | 50Hz | max. for thickness 0.35 mm | at 1 T |
4.12 W/kg Show Supplier Material materials with Typischer Kernverlust of 4.12 W/kg | 60Hz | max. for thickness 0.35 mm | at 1.5 T |
Technological properties
Property | ||
---|---|---|
Application areas | High permeability is particularly useful for applications such as ballasts and motors, because it makes it possible to build machines that meet the most stringent environmental regulations. High thermal conductivity is a significant advantage for large machines. | |
Coating | This high permeability grade is available non-insulated or varnished. | |
Other | The above properties are obtained without heat treatment after stamping. The material as supplied possesses all the required magnetic properties. |