Eigenschaften
Allgemein
| Property | Value |
|---|---|
Dichte | 7.6 g/cm³ Show Supplier Material materials with Dichte of 7.6 g/cm³ |
Mechanisch
| Property | Value | Comment |
|---|---|---|
Dehnung | 12 - 22 % Show Supplier Material materials with Dehnung of 12 - 22 % | A80 |
Härte, Vickers | 205 - 235 [-] Show Supplier Material materials with Härte, Vickers of 205 - 235 [-] | |
Number of bends | 2 [-] Show Supplier Material materials with Number of bends of 2 [-] | min. Guaranteed |
Streckgrenze | 395 - 435 MPa Show Supplier Material materials with Streckgrenze of 395 - 435 MPa | |
Yield to strength ratio | 0.78 - 0.83 [-] Show Supplier Material materials with Yield to strength ratio of 0.78 - 0.83 [-] | |
Zugfestigkeit | 505 - 545 MPa Show Supplier Material materials with Zugfestigkeit of 505 - 545 MPa |
Magnetisch
| Property | Value | Frequency | Comment |
|---|---|---|---|
Garantierte Polarisierung | 1.48 [-] Show Supplier Material materials with Garantierte Polarisierung of 1.48 [-] | min. | at 2500 A/m | |
1.59 [-] Show Supplier Material materials with Garantierte Polarisierung of 1.59 [-] | min. | at 5000 A/m | ||
1.69 [-] Show Supplier Material materials with Garantierte Polarisierung of 1.69 [-] | min. | at 10000 A/m | ||
Garantierter Kernverlust | 15 W/kg Show Supplier Material materials with Garantierter Kernverlust of 15 W/kg | 400Hz | max. at 1 T |
Stacking factor | 0.93 mm Show Supplier Material materials with Stacking factor of 0.93 mm | min. | Guaranteed | |
Typischer Kernverlust | 32 W/kg Show Supplier Material materials with Typischer Kernverlust of 32 W/kg | 700Hz | at 1 T |
38 W/kg Show Supplier Material materials with Typischer Kernverlust of 38 W/kg | 400Hz | max. at 1.5 T |
Technological properties
| Property | ||
|---|---|---|
| Application areas | This grade is designed for high speed rotating machines (100 to 5000 Hz). It allows minimisation of losses due to higher harmonics and clearly increases machine efficiency in the case of non-sinusoidal power supply. This thin, fully processed grade is also used when weight and volume reduction are of major importance, such as in medical or aviation applications. | |
| Coating | This high frequency grade is available non-insulated or varnished with a C5-type coating. | |
| Other | The above properties are obtained without heat treatment after stamping. The material as supplied possesses all the required magnetic properties. | |