Allgemein
Property | Value |
---|---|
Dichte | 7.85 g/cm³ Show Supplier Material materials with Dichte of 7.85 g/cm³ |
Mechanisch
Property | Value | Comment |
---|---|---|
Dehnung | 30 % Show Supplier Material materials with Dehnung of 30 % | min. | for thickness 0.50 mm | Transverse | A80 |
Härte, Vickers | 130 - 180 [-] Show Supplier Material materials with Härte, Vickers of 130 - 180 [-] | for thickness 0.50 mm |
Streckgrenze | 350 - 490 MPa Show Supplier Material materials with Streckgrenze of 350 - 490 MPa | for thickness 0.50 mm | Transverse |
Zugfestigkeit | 380 - 500 MPa Show Supplier Material materials with Zugfestigkeit of 380 - 500 MPa | for thickness 0.50 mm | Transverse |
Magnetisch
Property | Value | Frequency | Comment | ||
---|---|---|---|---|---|
Garantierte Polarisierung | 1.61 [-] Show Supplier Material materials with Garantierte Polarisierung of 1.61 [-] | min. | for thickness 0.50 mm | at 2500 A/m | |||
1.68 [-] Show Supplier Material materials with Garantierte Polarisierung of 1.68 [-] | min. | for thickness 0.50 mm | at 5000 A/m | ||||
1.79 [-] Show Supplier Material materials with Garantierte Polarisierung of 1.79 [-] | min. | for thickness 0.50 mm | at 10000 A/m | ||||
Garantierter Kernverlust | 4.5 W/kg Show Supplier Material materials with Garantierter Kernverlust of 4.5 W/kg | 50Hz | max. for thickness 0.50 mm | at 1.5 T | ||
Typischer Kernverlust | 1.9 W/kg Show Supplier Material materials with Typischer Kernverlust of 1.9 W/kg | 50Hz | max. for thickness 0.50 mm | at 1 T | ||
5.7 W/kg Show Supplier Material materials with Typischer Kernverlust of 5.7 W/kg | 60Hz | max. for thickness 0.50 mm | at 1.5 T | |||
Magnetic properties | The very high permeability grades (XP) offer excellent performance at 45°, with J2500 up to 1.79 T. Deviating from the standard Epstein test, we guarantee for these grades the average values measured in all directions of the sheet plane. These values are representative of the real material behaviour in a rotating machine. The magnetic properties given for the high permeability grades (P) refer to the standard Epstein test (mixture of L and T direction). |
Technological properties
Property | ||
---|---|---|
Application areas | This semi-processed high permeability grade is designed for motors, generators, transformers, converters and ballasts where higher efficiency is required. | |
Coating | As with the standard grades, the high permeability grade is available non-insulated. However, this high permeability grade can be supplied with an organic or inorganic-organic coating to meet higher insulating requirements. | |
Other | It needs no particular machine production process adjustments. |