Property | Value | Comment |
---|---|---|
Dehnung | 13 % Show Supplier Material materials with Dehnung of 13 % | min. | for thickness 1 mm | Transverse | A80 | Guaranteed |
25 - 35 % Show Supplier Material materials with Dehnung of 25 - 35 % | for thickness 1 mm | Transverse | A80 | Typical values | |
Härte, Vickers | 180 - 210 [-] Show Supplier Material materials with Härte, Vickers of 180 - 210 [-] | Typical values for thickness 1 mm |
Streckgrenze | 350 MPa Show Supplier Material materials with Streckgrenze of 350 MPa | min. | Guaranteed | Transverse |
400 - 440 MPa Show Supplier Material materials with Streckgrenze of 400 - 440 MPa | Typical values | Transverse | |
Yield to strength ratio | 0.74 - 0.79 [-] Show Supplier Material materials with Yield to strength ratio of 0.74 - 0.79 [-] | Typical values |
Zugfestigkeit | 425 MPa Show Supplier Material materials with Zugfestigkeit of 425 MPa | min. | Guaranteed |
530 - 570 MPa Show Supplier Material materials with Zugfestigkeit of 530 - 570 MPa | Typical values |
Magnetisch
Property | Value | Comment |
---|---|---|
Garantierte Polarisierung | 1.52 [-] Show Supplier Material materials with Garantierte Polarisierung of 1.52 [-] | min. | for thickness 1 mm | in DC at 5000 A/m |
1.81 [-] Show Supplier Material materials with Garantierte Polarisierung of 1.81 [-] | min. | for thickness 1 mm | in DC at 15000 A/m | |
Typische Polarisierung | 1.67 [-] Show Supplier Material materials with Typische Polarisierung of 1.67 [-] | min. | for thickness 1 mm | in DC at 5000 A/m |
1.86 [-] Show Supplier Material materials with Typische Polarisierung of 1.86 [-] | min. | for thickness 1 mm | in DC at 15000 A/m |
Technological properties
Property | ||
---|---|---|
Application areas | Cold rolled pole sheet grade is designed for large high-speed machines because of its excellent combination of mechanical strength and magnetic performance. | |
Other | These properties are obtained without heat treatment after stamping. The material as supplied possesses all the required magnetic properties. |