Abmessung
Property | Value |
---|---|
Dimensions | Please feel free to check the figure on the right side of the material page for more details. |
Mechanisch
Property | Value | Comment |
---|---|---|
Dehnung | 12 % Show Supplier Material materials with Dehnung of 12 % | min. | for thickness 0.35-0.5 mm | A80 |
14 % Show Supplier Material materials with Dehnung of 14 % | min. | for thickness 0.5-0.7 mm | A80 | |
16 % Show Supplier Material materials with Dehnung of 16 % | min. | for thickness 0.7-6 mm | A80 | |
Streckgrenze | 390 MPa Show Supplier Material materials with Streckgrenze of 390 MPa | min. | for thickness 0.3-6 mm |
Zugfestigkeit | 460 MPa Show Supplier Material materials with Zugfestigkeit of 460 MPa | min. | for thickness 0.3-6 mm |
Chemical properties
Property | Value | Comment |
---|---|---|
Kohlenstoff | 0.2 % Show Supplier Material materials with Kohlenstoff of 0.2 % | max. |
Mangan | 1.7 % Show Supplier Material materials with Mangan of 1.7 % | max. |
Phosphor | 0.1 % Show Supplier Material materials with Phosphor of 0.1 % | max. |
Schwefel | 0.045 % Show Supplier Material materials with Schwefel of 0.045 % | max. |
Silizium | 0.6 % Show Supplier Material materials with Silizium of 0.6 % | max. |
Technological properties
Property | ||
---|---|---|
Application areas | ArcelorMittal's hot dip galvanised steels can be used in a very wide range of applications for industrial markets, both indoors and outdoors. Some of the most common applications are: Zinc hot dip galvanised steel is suitable for contact with foodstuffs under certain conditions, as specified in the Regulation (EC) No. 1935/2004 and French standard NF A 36-712-1. Please contact us for further information on this subject. | |
Chemical composition | If, by agreement at the time of enquiry and order, other chemical elements are added, they shall be mentioned on the inspection document which may need a change of classification. | |
Coating | ||
Other | Storage Galvanised strip are usually supplied passivated or oiled to temporarily limit any risk of white rust formation. During transport and storage, all necessary precautions must be taken to keep the material dry and to prevent the formation of condensation. Improved protection can be achieved by the application of an Easyfilm® thin organic coating (please see data sheet E80 for the specific properties of Easyfilm®). Forming and joining The forming and joining techniques currently used for uncoated steel are also suitable for galvanised steel. It is essential to select a coating thickness that is compatible with the forming and joining processes envisaged, without compromising the desired degree of corrosion protection. Painting Hot dip galvanised steel can be painted after degreasing and surface treatment when supplied oiled. If an Easyfilm® thin organic coating has been applied, they can be painted directly, without any prior surface treatment. However, the paint must be compatible with the Easyfilm® resin. | |
Welding | In electrical resistance welding, the welding current must be suitably regulated and regularly adjusted. Electrode life can be extended by regularly stepping up the welding current and periodically dressing (machining) the electrodes. |