Eigenschaften
Allgemein
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dichte | 23.0 °C | 1.65 g/cm³ Show Supplier Material materials with Dichte of 1.65 g/cm³ | at 230°C |
Mechanisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Biegefestigkeit | 23.0 °C | 750 MPa Show Supplier Material materials with Biegefestigkeit of 750 MPa | ISO 14125, 2mm/min |
Biegemodul | 23.0 °C | 31 GPa Show Supplier Material materials with Biegemodul of 31 GPa | ISO 14125, 2mm/min |
Dehnung | 23.0 °C | 2.5 % Show Supplier Material materials with Dehnung of 2.5 % | ISO 527-5/Tape, 5mm/min |
Elastizitätsmodul | 23.0 °C | 31 GPa Show Supplier Material materials with Elastizitätsmodul of 31 GPa | ISO 527-5/Tape, 1mm/min |
Interlaminare Scherfestigkeit | 23.0 °C | 23 MPa Show Supplier Material materials with Interlaminare Scherfestigkeit of 23 MPa | ISO 14130, 1mm/min |
Zugfestigkeit | 23.0 °C | 700 MPa Show Supplier Material materials with Zugfestigkeit of 700 MPa | ISO 527-5/Tape, 5 mm/min |
Thermisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Koeffizient der thermischen Ausdehnung | 23.0 °C | 1.3E-5 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 1.3E-5 1/K | ISO 11359, 23-500°C at 50°C/min |
Schmelzpunkt | 205 °C Show Supplier Material materials with Schmelzpunkt of 205 °C | ISO 11357, 100°C/min | |
thermischer Ausdehnungskoeffizient, transversal | 23.0 °C | 1.2E-4 1/K Show Supplier Material materials with thermischer Ausdehnungskoeffizient, transversal of 1.2E-4 1/K | ISO 11359, 23-500°C at 50°C/min |
Technological properties
| Property | ||
|---|---|---|
| Application areas | METALENTA, a unidirectionally reinforced fiberglass tape, is applied for creation an external protective and reinforcing fiberglass coating of steel pipelines with a diameter 219 to 1420 mm with an external polymer anticorrosive coating. Fiberglass coating is designated to protect the anticorrosive polymer coating from mechanical stress during the construction, operation, repair and reconstruction of the pipeline. The material is also applied for creation an external protective layer of extrusion pipes and cables to prevent surface damage during installation and operation and for creation a reinforcing layer to strengthen the structure in the production of composite pipes, sheets, panels, honeycomb structures, etc. | |
| Fillers | Glass Fiber | |