Eigenschaften
Allgemein
| Property | Temperature | Value | Testing Standard |
|---|---|---|---|
Dichte | 25 °C | 1.02 g/cm³ Show Supplier Material materials with Dichte of 1.02 g/cm³ | ISO 1183-1 |
Mechanisch
| Property | Temperature | Value | Testing Standard | Comment |
|---|---|---|---|---|
Biegefestigkeit | 66 MPa Show Supplier Material materials with Biegefestigkeit of 66 MPa | ISO 178 | 2 mm/min | |
Biegemodul | 1.9 GPa Show Supplier Material materials with Biegemodul of 1.9 GPa | ISO 178 | 2 mm/min | |
Dehnung | 15 % Show Supplier Material materials with Dehnung of 15 % | ISO 527-1/2 | min. | 50 mm/min | |
Elastizitätsmodul | 1.9 GPa Show Supplier Material materials with Elastizitätsmodul of 1.9 GPa | ISO 527-1/2 | 1 mm/min | |
Hardness, Ball Indentation | 81 MPa Show Supplier Material materials with Hardness, Ball Indentation of 81 MPa | ISO 2039-1 | ||
Schlagfestigkeit, Charpy gekerbt | -30 °C | 21 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 21 kJ/m² | ISO 179-1eA | |
23 °C | 31 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 31 kJ/m² | ISO 179-1eA | ||
Schlagzähigkeit, Izod gekerbt | -30 °C | 20 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Izod gekerbt of 20 kJ/m² | ISO 180-1A | |
23 °C | 25 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Izod gekerbt of 25 kJ/m² | ISO 180-1A | ||
Streckgrenze | 38 MPa Show Supplier Material materials with Streckgrenze of 38 MPa | ISO 527-1/2 | 50 mm/min |
Thermisch
| Property | Value | Testing Standard | Comment | ||
|---|---|---|---|---|---|
Koeffizient der thermischen Ausdehnung | 0.0001 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 0.0001 1/K | ISO 11359-1/2 | 23 to 55°C | ||
Vicat-Erweichungstemperatur | 95 °C Show Supplier Material materials with Vicat-Erweichungstemperatur of 95 °C | ISO 306 | 50 N | 50°C/h | ||
97 °C Show Supplier Material materials with Vicat-Erweichungstemperatur of 97 °C | ISO 306 | 50 N | 120°C/h | |||
Entflammbarkeit | At thickness 1.6 mm UL 94: HB. Burning rate US-FMVSS (2mm): < 40 mm/min according to ISO 3795 | ||||
Rheological Properties
| Property | Value | Testing Standard | Comment |
|---|---|---|---|
Schmelzvolumenflussrate | 14 cm³/10min Show Supplier Material materials with Schmelzvolumenflussrate of 14 cm³/10min | ISO 1133 | 220°C/10Kg |
Schrumpfung | 0.6 - 0.7 % Show Supplier Material materials with Schrumpfung of 0.6 - 0.7 % | ISO 294-4 | 60x60x2 mm |
0.6 - 0.7 % Show Supplier Material materials with Schrumpfung of 0.6 - 0.7 % | ISO 294-4 | 60x60x2 mm, Transverse |
Technological properties
| Property | ||
|---|---|---|
| Certifications | UL Certificate | |
| Color | White to slightly yellowish. | |
| Handling recommendations | Please see the Material Safety Data Sheet for relevant health & safety information. | |
| Other | Control measurements in other places may issue different results due to influences of machinery, equipment, test method or storage conditions. | |
| Processing methods | Injection molding-melt temperature: 240 ºC according to ISO 294 Injection molding-mold temperature: 70 ºC according to ISO 294 Injection molding-injection velocity: 240 mm/s according to ISO 294 | |