Allgemein
Property | Temperature | Value | Testing Standard |
---|---|---|---|
Dichte | 25 °C | 1.07 g/cm³ Show Supplier Material materials with Dichte of 1.07 g/cm³ | ISO 1183-1 |
Mechanisch
Property | Temperature | Value | Testing Standard | Comment |
---|---|---|---|---|
Biegefestigkeit | 73 MPa Show Supplier Material materials with Biegefestigkeit of 73 MPa | ISO 178 | 2 mm/min | |
Biegemodul | 2.1 GPa Show Supplier Material materials with Biegemodul of 2.1 GPa | ISO 527-1/2 | 2 mm/min | |
Dehnung | 30 % Show Supplier Material materials with Dehnung of 30 % | ISO 527-1/2 | 50 mm/min | |
Elastizitätsmodul | 2.1 GPa Show Supplier Material materials with Elastizitätsmodul of 2.1 GPa | ISO 527-1/2 | 1 mm/min | |
Elongation at yield | 4 % Show Supplier Material materials with Elongation at yield of 4 % | ISO 527-1/2 | 50 mm/min | |
Hardness, Ball Indentation | 103 MPa Show Supplier Material materials with Hardness, Ball Indentation of 103 MPa | ISO 2039-1 | ||
Schlagfestigkeit, Charpy gekerbt | -30 °C | 24 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 24 kJ/m² | ISO 179-1eA | |
23 °C | 50 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 50 kJ/m² | ISO 179-1eA | ||
Schlagzähigkeit, Izod gekerbt | -30 °C | 26 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Izod gekerbt of 26 kJ/m² | ISO 180-1A | |
23 °C | 58 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Izod gekerbt of 58 kJ/m² | ISO 180-1A | ||
Streckgrenze | 44 MPa Show Supplier Material materials with Streckgrenze of 44 MPa | ISO 527-1/2 | 50 mm/min |
Thermisch
Property | Value | Testing Standard | Pressure | Comment | |||
---|---|---|---|---|---|---|---|
Koeffizient der thermischen Ausdehnung | 9.5e-05 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 9.5e-05 1/K | ISO 11359-1/2 | 23 to 55°C | ||||
Vicat-Erweichungstemperatur | 113 °C Show Supplier Material materials with Vicat-Erweichungstemperatur of 113 °C | ISO 306 | B50 | 50°C/h | ||||
Wärmeformbeständigkeitstemperatur | 95 °C Show Supplier Material materials with Wärmeformbeständigkeitstemperatur of 95 °C | ISO 75-1/2 | 1.8 MPa | ||||
113 °C Show Supplier Material materials with Wärmeformbeständigkeitstemperatur of 113 °C | ISO 75-1/2 | 0.45 MPa | |||||
Entflammbarkeit | At thickness 1.6 mm UL 94: HB. Burning rate US-FMVSS (200x105x2 mm): < 50 mm/min according to ISO 3795 |
Rheological Properties
Property | Value | Testing Standard | Comment |
---|---|---|---|
Schmelzvolumenflussrate | 26 cm³/10min Show Supplier Material materials with Schmelzvolumenflussrate of 26 cm³/10min | ISO 1133 | 260°C/5Kg |
Schrumpfung | 0.55 - 0.65 % Show Supplier Material materials with Schrumpfung of 0.55 - 0.65 % | ISO 294-4 | 60x60x2 mm |
0.55 - 0.65 % Show Supplier Material materials with Schrumpfung of 0.55 - 0.65 % | ISO 294-4 | 60x60x2 mm, Transverse |
Technological properties
Property | ||
---|---|---|
Certifications | UL Certificate | |
Chemical composition | Acrylonitrile-butadiene-styrene (ABS) copolymer modified with polycarbonate and poly(styrene-co-maleimide). | |
Color | White to slightly yellowish. | |
Handling recommendations | Please see the Material Safety Data Sheet for relevant health & safety information. | |
Other | Control measurements in other places may issue different results due to influences of machinery, equipment, test method or storage conditions. | |
Processing methods | Injection molding-melt temperature: 240 ºC according to ISO 294 Injection molding-mold temperature: 70 ºC according to ISO 294 Injection molding-injection velocity: 240 mm/s according to ISO 294 |