Eigenschaften
Allgemein
| Property | Temperature | Value | Testing Standard |
|---|---|---|---|
Dichte | 25 °C | 1.04 g/cm³ Show Supplier Material materials with Dichte of 1.04 g/cm³ | ISO 1183-1 |
Mechanisch
| Property | Temperature | Value | Testing Standard | Comment |
|---|---|---|---|---|
Biegefestigkeit | 66 MPa Show Supplier Material materials with Biegefestigkeit of 66 MPa | ISO 178 | 2 mm/min | |
Biegemodul | 2.4 GPa Show Supplier Material materials with Biegemodul of 2.4 GPa | ISO 527-1/2 | 2 mm/min | |
Dehnung | 17 % Show Supplier Material materials with Dehnung of 17 % | ISO 527-1/2 | 50 mm/min | |
Elastizitätsmodul | 2.2 GPa Show Supplier Material materials with Elastizitätsmodul of 2.2 GPa | ISO 527-1/2 | 1 mm/min | |
Hardness, Ball Indentation | 105 MPa Show Supplier Material materials with Hardness, Ball Indentation of 105 MPa | ISO 2039-1 | ||
Schlagfestigkeit, Charpy gekerbt | 23 °C | 13 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 13 kJ/m² | ISO 179-1eA | |
Schlagzähigkeit, Izod gekerbt | -30 °C | 8 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Izod gekerbt of 8 kJ/m² | ISO 180-1A | |
23 °C | 13 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Izod gekerbt of 13 kJ/m² | ISO 180-1A | ||
Streckgrenze | 42 MPa Show Supplier Material materials with Streckgrenze of 42 MPa | ISO 527-1/2 | 50 mm/min |
Thermisch
| Property | Value | Testing Standard | Pressure | Comment | |||
|---|---|---|---|---|---|---|---|
Koeffizient der thermischen Ausdehnung | 9.2e-05 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 9.2e-05 1/K | ISO 11359-1/2 | 23 to 55°C | ||||
Vicat-Erweichungstemperatur | 112 °C Show Supplier Material materials with Vicat-Erweichungstemperatur of 112 °C | ISO 306 | B50 | 50°C/h | ||||
114 °C Show Supplier Material materials with Vicat-Erweichungstemperatur of 114 °C | ISO 306 | B120 | 120°C/h | |||||
Wärmeformbeständigkeitstemperatur | 104 °C Show Supplier Material materials with Wärmeformbeständigkeitstemperatur of 104 °C | ISO 75-1/2 | 1.8 MPa | ||||
112 °C Show Supplier Material materials with Wärmeformbeständigkeitstemperatur of 112 °C | ISO 75-1/2 | 0.45 MPa | |||||
Entflammbarkeit | At thickness 1.6 mm UL 94: HB. Burning rate US-FMVSS (200x105x2 mm): < 55 mm/min according to ISO 3795 | ||||||
Rheological Properties
| Property | Value | Testing Standard | Comment |
|---|---|---|---|
Schmelzvolumenflussrate | 9 cm³/10min Show Supplier Material materials with Schmelzvolumenflussrate of 9 cm³/10min | ISO 1133 | 220°C/10Kg |
Schrumpfung | 0.35 - 0.4 % Show Supplier Material materials with Schrumpfung of 0.35 - 0.4 % | ISO 294-4 | 60x60x2 mm |
0.4 - 0.55 % Show Supplier Material materials with Schrumpfung of 0.4 - 0.55 % | ISO 294-4 | 60x60x2 mm, Transverse |
Technological properties
| Property | ||
|---|---|---|
| Certifications | UL Certificate | |
| Chemical composition | Acrylonitrile-butadiene-styrene (ABS) copolymer modified with poly(styrene-co-maleimide) (SMI). | |
| Color | White to slightly yellowish. | |
| Handling recommendations | Please see the Material Safety Data Sheet for relevant health & safety information. | |
| Other | Control measurements in other places may issue different results due to influences of machinery, equipment, test method or storage conditions. | |
| Processing methods | Injection molding-melt temperature: 240 ºC according to ISO 294 Injection molding-mold temperature: 70 ºC according to ISO 294 Injection molding-injection velocity: 240 mm/s according to ISO 294 | |