Eigenschaften
Allgemein
| Property | Temperature | Value | Testing Standard |
|---|---|---|---|
Dichte | 25 °C | 1.05 g/cm³ Show Supplier Material materials with Dichte of 1.05 g/cm³ | ISO 1183-1 |
Mechanisch
| Property | Temperature | Value | Testing Standard | Comment |
|---|---|---|---|---|
Biegefestigkeit | 65 MPa Show Supplier Material materials with Biegefestigkeit of 65 MPa | ISO 178 | 2 mm/min | |
Biegemodul | 2.2 GPa Show Supplier Material materials with Biegemodul of 2.2 GPa | ISO 527-1/2 | 2 mm/min | |
Elastizitätsmodul | 2.3 GPa Show Supplier Material materials with Elastizitätsmodul of 2.3 GPa | ISO 527-1/2 | 1 mm/min | |
Hardness, Ball Indentation | 103 MPa Show Supplier Material materials with Hardness, Ball Indentation of 103 MPa | ISO 2039-1 | ||
Schlagfestigkeit, Charpy gekerbt | -30 °C | 11 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 11 kJ/m² | ISO 179-1eA | |
23 °C | 18 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 18 kJ/m² | ISO 179-1eA | ||
Schlagzähigkeit, Charpy ungekerbt | -30 °C | 80 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Charpy ungekerbt of 80 kJ/m² | ISO 179-1eU | |
23 °C | 100 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Charpy ungekerbt of 100 kJ/m² | ISO 179-1eU | ||
Schlagzähigkeit, Izod gekerbt | -30 °C | 12 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Izod gekerbt of 12 kJ/m² | ISO 180-1A | |
23 °C | 18 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Izod gekerbt of 18 kJ/m² | ISO 180-1A | ||
Streckgrenze | 41 MPa Show Supplier Material materials with Streckgrenze of 41 MPa | ISO 527-1/2 | 50 mm/min |
Thermisch
| Property | Value | Testing Standard | Pressure | Comment |
|---|---|---|---|---|
Koeffizient der thermischen Ausdehnung | 0.0001 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 0.0001 1/K | ISO 11359-1/2 | 23 to 55°C | |
0.0001 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 0.0001 1/K | ISO 11359-1/2 | 23 to 55°C, Transverse | ||
Vicat-Erweichungstemperatur | 95 °C Show Supplier Material materials with Vicat-Erweichungstemperatur of 95 °C | ISO 306 | 50 N | 50°C/h | |
97 °C Show Supplier Material materials with Vicat-Erweichungstemperatur of 97 °C | ISO 306 | 50 N | 120°C/h | ||
Wärmeformbeständigkeitstemperatur | 92 °C Show Supplier Material materials with Wärmeformbeständigkeitstemperatur of 92 °C | ISO 75-1/2 | 1.8 MPa | |
97 °C Show Supplier Material materials with Wärmeformbeständigkeitstemperatur of 97 °C | ISO 75-1/2 | 0.45 MPa |
Elektrisch
| Property | Value | Frequency | Testing Standard | Comment |
|---|---|---|---|---|
Dielektrizitätskonstante | 2.9 [-] Show Supplier Material materials with Dielektrizitätskonstante of 2.9 [-] | 100Hz | IEC 60250 | |
2.9 [-] Show Supplier Material materials with Dielektrizitätskonstante of 2.9 [-] | 1MHz | IEC 60250 | ||
Durchschlagfestigkeit | 35 kV/mm Show Supplier Material materials with Durchschlagfestigkeit of 35 kV/mm | IEC 60243-1 | 1 mm | |
Surface resistivity | 1e+16 Ω/sq Show Supplier Material materials with Surface resistivity of 1e+16 Ω/sq | |||
Verlustfaktor | 0.0073 [-] Show Supplier Material materials with Verlustfaktor of 0.0073 [-] | 100Hz | IEC 60250 | |
0.009 [-] Show Supplier Material materials with Verlustfaktor of 0.009 [-] | 1MHz | IEC 60250 | ||
Volume resistivity | 1e+18 Ω·cm Show Supplier Material materials with Volume resistivity of 1e+18 Ω·cm | IEC 60093 |
Rheological Properties
| Property | Value | Testing Standard | Comment |
|---|---|---|---|
Schmelzvolumenflussrate | 32 cm³/10min Show Supplier Material materials with Schmelzvolumenflussrate of 32 cm³/10min | ISO 1133 | 220°C/10Kg |
Schrumpfung | 0.6 % Show Supplier Material materials with Schrumpfung of 0.6 % | ISO 2577 | 150x105x3 |
0.6 % Show Supplier Material materials with Schrumpfung of 0.6 % | ISO 2577 | 150x105x3, Transverse |
Technological properties
| Property | ||
|---|---|---|
| Certifications | UL Certificate | |
| Handling recommendations | Please see the Material Safety Data Sheet for relevant health & safety information. | |
| Other | Control measurements in other places may issue different results due to influences of machinery, equipment, test method or storage conditions. | |
| Processing methods | Injection molding-melt temperature: 240 ºC according to ISO 294 Injection molding-mold temperature: 80 ºC according to ISO 294 Injection molding-injection velocity: 240 mm/s according to ISO 294 | |