Allgemein
Mechanisch
Property | Temperature | Value | Comment |
---|---|---|---|
Biegefestigkeit | 23.0 °C | 265 MPa Show Supplier Material materials with Biegefestigkeit of 265 MPa | ISO 178 (2mm/min) |
Biegemodul | 23.0 °C | 10.5 GPa Show Supplier Material materials with Biegemodul of 10.5 GPa | ISO 178 (2mm/min) |
Dehnung | 23.0 °C | 3 % Show Supplier Material materials with Dehnung of 3 % | ISO 527-2 (5mm/min) |
Elastizitätsmodul | 23.0 °C | 12 GPa Show Supplier Material materials with Elastizitätsmodul of 12 GPa | ISO 527-2 (1mm/min) |
Schlagfestigkeit, Charpy gekerbt | 23.0 °C | 16 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 16 kJ/m² | ISO 179/1eA |
Schlagzähigkeit, Charpy ungekerbt | 23.0 °C | 95 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Charpy ungekerbt of 95 kJ/m² | ISO 179/1eU |
Schlagzähigkeit, Izod gekerbt | 23.0 °C | 15 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Izod gekerbt of 15 kJ/m² | ISO 180/1A |
Schlagzähigkeit, Izod ungekerbt | 23.0 °C | 90 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Izod ungekerbt of 90 kJ/m² | ISO 180/1U |
Zugfestigkeit | 23.0 °C | 200 MPa Show Supplier Material materials with Zugfestigkeit of 200 MPa | ISO 527-2 (5mm/min) |
Thermisch
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Aschegehalt | 23.0 °C | 35 % Show Supplier Material materials with Aschegehalt of 35 % | ISO 3451-4 | ||
Heat deflection temperature, 0.45 MPa | 255 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 255 °C | ISO 75-2/B | |||
Heat deflection temperature, 1.80 MPa | 250 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 250 °C | ISO 75-2/A | |||
Schmelzpunkt | 260 °C Show Supplier Material materials with Schmelzpunkt of 260 °C | ISO 3146 | |||
Entflammbarkeit | UL94 (0.8mm) HB |
Elektrisch
Property | Temperature | Value | Comment |
---|---|---|---|
Kriechstromfestigkeit | 23.0 °C | 400 V Show Supplier Material materials with Kriechstromfestigkeit of 400 V | EN 60112 |
Surface resistivity | 23.0 °C | 1.00E+14 Ω/sq Show Supplier Material materials with Surface resistivity of 1.00E+14 Ω/sq | ASTM D257 |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Application areas | Eplamid 66 GFH compounds are used in all sectors of industry especially automotive under the hood applications, offering an excellent balance of thermal and mechanical properties. Its good for long term heat resistance as well as hyrdolysis resistant applications. | |
Fillers | 35% Glass Fiber | |
Other | Laboratory conditions are 23 ±2°C and 45-55 % RH. |