Eigenschaften
Allgemein
| Property | Value | Comment |
|---|---|---|
Dichte | 1.13 g/cm³ Show Supplier Material materials with Dichte of 1.13 g/cm³ | OECD 109 (neat resin) |
Mechanisch
| Property | Value | Comment |
|---|---|---|
Biegefestigkeit | 115.0 MPa Show Supplier Material materials with Biegefestigkeit of 115.0 MPa | DIN EN ISO 178 (neat resin) |
Biegemodul | 3.3 GPa Show Supplier Material materials with Biegemodul of 3.3 GPa | DIN EN ISO 178 (neat resin) |
Dehnung | 2.3 % Show Supplier Material materials with Dehnung of 2.3 % | DIN EN ISO 527-2 (neat resin) |
Elastizitätsmodul | 3.4 GPa Show Supplier Material materials with Elastizitätsmodul of 3.4 GPa | DIN EN ISO 527-2 (neat resin) |
Flexural strain | 3.6 % Show Supplier Material materials with Flexural strain of 3.6 % | DIN EN ISO 178 (neat resin) |
Interlaminare Scherfestigkeit | 80 MPa Show Supplier Material materials with Interlaminare Scherfestigkeit of 80 MPa | DIN EN ISO 14130 (Laminate) |
90 MPa Show Supplier Material materials with Interlaminare Scherfestigkeit of 90 MPa | DIN EN ISO 14130 (Laminate) | |
Plane-Strain Fracture Toughnes | 1.7 MPa·√m Show Supplier Material materials with Plane-Strain Fracture Toughnes of 1.7 MPa·√m | ASTM D 5045-99 |
Poissonzahl | 0.34 [-] Show Supplier Material materials with Poissonzahl of 0.34 [-] | DIN EN ISO 527-1 (neat resin) |
Zugfestigkeit | 85.0 MPa Show Supplier Material materials with Zugfestigkeit of 85.0 MPa | DIN EN ISO 527-2 (neat resin) |
Thermisch
| Property | Value | Comment |
|---|---|---|
Exothermic Peak | 166 °C Show Supplier Material materials with Exothermic Peak of 166 °C | DSC [10K/min] (After prepreg step) |
168 °C Show Supplier Material materials with Exothermic Peak of 168 °C | DSC [10K/min] (After prepreg step) | |
Gel time | 350 sec Show Supplier Material materials with Gel time of 350 sec | Geltimer (Plate) at 140°C |
450 sec Show Supplier Material materials with Gel time of 450 sec | Geltimer (Plate) at 140°C | |
Glasübergangstemperatur | 140.0 °C Show Supplier Material materials with Glasübergangstemperatur of 140.0 °C | DIN EN ISO 11357-2 (neat resin) |
Koeffizient der thermischen Ausdehnung | 0.00006 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 0.00006 1/K | 20 to 130°C |
Rheological Properties
| Property | Value | Comment |
|---|---|---|
Schrumpfung | 0.9 % Show Supplier Material materials with Schrumpfung of 0.9 % | pVT Method (neat resin) |
Viskosität | 0.2 Pa·s Show Supplier Material materials with Viskosität of 0.2 Pa·s | ISO 3219 | OECD 114 (neat resin) |
4 Pa·s Show Supplier Material materials with Viskosität of 4 Pa·s | ISO 3219 | OECD 114 (neat resin) |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Lower volume and automated production of structural FRP components like leaf springs (PCM - Technology) and autoclave applications, exterior or interior surface applications. Curing speed can be adapted by catalyst. | |
| Color | 0 - 1.5 Gardner according to DIN EN ISO 4630 | |