Eigenschaften
Mechanisch
| Property | Value | Condition | Comment |
|---|---|---|---|
Biegefestigkeit | 545.0 MPa Show Supplier Material materials with Biegefestigkeit of 545.0 MPa | The properties of cured SMC material (68.1 % carbon fiber mass fraction) | EN ISO 14125 (cured SMC material) |
Biegemodul | 39.0 GPa Show Supplier Material materials with Biegemodul of 39.0 GPa | The properties of cured SMC material (68.1 % carbon fiber mass fraction) | EN ISO 14125 (cured SMC material) |
Dehnung | 0.7 % Show Supplier Material materials with Dehnung of 0.7 % | The properties of cured SMC material (68.1 % carbon fiber mass fraction) | DIN EN ISO 527-4 (cured SMC material) |
Druckfestigkeit | 323.0 MPa Show Supplier Material materials with Druckfestigkeit of 323.0 MPa | The properties of cured SMC material (68.1 % carbon fiber mass fraction) | EN ISO 14126 (cured SMC material) |
Elastizitätsmodul | 44.0 GPa Show Supplier Material materials with Elastizitätsmodul of 44.0 GPa | The properties of cured SMC material (68.1 % carbon fiber mass fraction) | DIN EN ISO 527-4 (cured SMC material) |
Flexural strain | 1.8 % Show Supplier Material materials with Flexural strain of 1.8 % | The properties of cured SMC material (68.1 % carbon fiber mass fraction) | EN ISO 14125 (cured SMC material) |
Kompressionsmodul | 35100.0 MPa Show Supplier Material materials with Kompressionsmodul of 35100.0 MPa | The properties of cured SMC material (68.1 % carbon fiber mass fraction) | EN ISO 14126 (cured SMC material) |
Schlagzähigkeit, Charpy ungekerbt | 107.0 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Charpy ungekerbt of 107.0 kJ/m² | The properties of cured SMC material (68.1 % carbon fiber mass fraction) | EN ISO 179-1 (cured SMC material) |
Zugfestigkeit | 263.0 MPa Show Supplier Material materials with Zugfestigkeit of 263.0 MPa | The properties of cured SMC material (68.1 % carbon fiber mass fraction) | DIN EN ISO 527-4 (cured SMC material) |
Rheological Properties
| Property | Value | Condition | Comment |
|---|---|---|---|
Viskosität | 0.5 Pa·s Show Supplier Material materials with Viskosität of 0.5 Pa·s | The properties of cured SMC material (68.1 % carbon fiber mass fraction) | (neat resin) |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Semi-structural parts, Supporting structures, structural lightweight applications, Exterior / Interior parts | |
| Fillers | Carbon Fiber | |
| Processing methods | The molding condition for SMC sheets: Molding pressure: 100-200 bar, Molding temperature: 150°C, Molding coverage: 50-80% and Curing time: 3-4 minutes | |