Eigenschaften
Allgemein
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dichte | 23.0 °C | 1.28 g/cm³ Show Supplier Material materials with Dichte of 1.28 g/cm³ | ISO1183 |
Mechanisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Biegefestigkeit | 23.0 °C | 200 MPa Show Supplier Material materials with Biegefestigkeit of 200 MPa | ISO178 |
Biegemodul | 23.0 °C | 8 GPa Show Supplier Material materials with Biegemodul of 8 GPa | ISO178 |
Dehnung | 23.0 °C | 7 % Show Supplier Material materials with Dehnung of 7 % | ISO527 |
Schlagfestigkeit, Charpy gekerbt | -30.0 °C | 13 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 13 kJ/m² | ISO179 |
23.0 °C | 18 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 18 kJ/m² | ISO179 | |
Zugfestigkeit | 23.0 °C | 145 MPa Show Supplier Material materials with Zugfestigkeit of 145 MPa | ISO527 |
Thermisch
| Property | Value | Comment |
|---|---|---|
Heat deflection temperature, 1.80 MPa | 175 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 175 °C | ISO75 |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Automotive lightweight components, Tubing connection, Sport health equipment | |
| Fillers | 30% Glass Fiber | |
| Processing methods | Drying Temperature: 80-85°C, Drying Time: 3-4 hr, Rear Temperature: 210°C, Middle Temperature: 220°C, Front Temperature: 230°C, Nozzle Temperature: 220°C, Mold Temperature: 60-80°C, Injection Pressure: 80-100 MPa | |