Allgemein
Property | Temperature | Value | Comment |
---|---|---|---|
Dichte | 23.0 °C | 1.37 g/cm³ Show Supplier Material materials with Dichte of 1.37 g/cm³ | ISO1183 |
Mechanisch
Property | Temperature | Value | Comment |
---|---|---|---|
Biegefestigkeit | 23.0 °C | 220 MPa Show Supplier Material materials with Biegefestigkeit of 220 MPa | ISO178 |
Biegemodul | 23.0 °C | 9.5 GPa Show Supplier Material materials with Biegemodul of 9.5 GPa | ISO178 |
Dehnung | 23.0 °C | 6 % Show Supplier Material materials with Dehnung of 6 % | ISO527 |
Schlagfestigkeit, Charpy gekerbt | -30.0 °C | 13 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 13 kJ/m² | ISO179 |
23.0 °C | 20 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 20 kJ/m² | ISO179 | |
Zugfestigkeit | 23.0 °C | 160 MPa Show Supplier Material materials with Zugfestigkeit of 160 MPa | ISO527 |
Thermisch
Property | Value | Comment |
---|---|---|
Heat deflection temperature, 1.80 MPa | 185 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 185 °C | ISO75 |
Technological properties
Property | ||
---|---|---|
Application areas | Automotive lightweight components, Tubing connection, Sport health equipment | |
Fillers | 40% Glass Fiber | |
Processing methods | Drying Temperature: 80-85°C, Drying Time: 3-4 hr, Rear Temperature: 210°C, Middle Temperature: 220°C, Front Temperature: 230°C, Nozzle Temperature: 220°C, Mold Temperature: 60-80°C, Injection Pressure: 80-100 MPa |