NiAl 80/20 Wire

Want to keep this datasheet? Save it now in your required format

Description

Wire 80% Ni and 20% Al: hpulcas has developed a process, where a NiAl wire is made from both nickel and aluminum strips, resulting in a highly reduced input of oxides. Whereas such a wire could have been produced before, it could not have been recrystallization annealed, as the recrystallization temperature of Ni 200 is 690 to 720 °C, whereas pure aluminum melts at 660 °C. the recrystallization temperature of high purity Ni hpulcas is lower and thus the wire can be annealed and various diameters can be produced through drawing and interim annealing.

Diese Materialdaten wurden von Hpulcas GmbH zur Verfügung gestellt

Alle Daten beziehen sich auf Raumtemperatur soweit nicht anderweitig spezifiziert. SI Einheiten werden verwendt soweit nicht anderweitig spezifiziert.
Äquivalente Standards sind ähnlich zu einem oder mehreren Standards die der Anbieter angegeben hat. Manche äquivalente Standards können strikter sein oder außerhalb der Bedingungen des ursprünglichen Standards.

Ashby charts

All categories

Eigenschaften

Abmessung

Property	Value
Dimensions	3.2 mm and 1.6 mm; various dimensions can be also customized

Chemical properties

Property	Value
Aluminium	20 % Show Supplier Material materials with Aluminium of 20 %
Nickel	80 % Show Supplier Material materials with Nickel of 80 %

Technological properties

Property
Application areas	thermal sprying NiAl, coating layer for corrosion resistance, coating layer for high temperature resistance, corrosion protection at high temperatures, coating layer for cavitation erossion resistance, repair worn/eroded turbine blades, coating layer for abrasion resistance, coating layer for wear resistance, bond coat for subsequent thermal spray topcoats/ceramic, coating on moulds in the glass industry
Heat Treatment	Hardened
Processing history	The NiAl 80/20 wires are made by folding layered metal strips. An inserted aluminum strip replaces the commonly used aluminum powder. Ni and Al strips are jointly formed together by means of profile rolling. The produced raw NiAl round form wire is drawn to the required diameter by wire drawing and intermediate annealing. special drawing dies are used to prevent the nickel top layer from cracking.
Surface Finish	Blank/Bare surface