Mechanisch
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Druckfestigkeit | 23.0 °C | 643 MPa Show Material materials with Druckfestigkeit of 643 MPa | ASTM D6641 | ||
Druckfestigkeit, transversal | 23.0 °C | 679 MPa Show Material materials with Druckfestigkeit, transversal of 679 MPa | ASTM D6641 | ||
Elastizitätsmodul | 23.0 °C | 65 GPa Show Material materials with Elastizitätsmodul of 65 GPa | ASTM D3039 | ||
Elastizitätsmodul, transversal | 23.0 °C | 66 GPa Show Material materials with Elastizitätsmodul, transversal of 66 GPa | ASTM D3039 | ||
Shear modulus, G₁₂ | 23.0 °C | 4.5 GPa Show Material materials with Shear modulus, G₁₂ of 4.5 GPa | ASTM D5379 | ||
Shear strength, τ₁₂ | 23.0 °C | 84 MPa Show Material materials with Shear strength, τ₁₂ of 84 MPa | |||
Shear strength, τ₁₃ | 25.0 °C | 74 MPa Show Material materials with Shear strength, τ₁₃ of 74 MPa | ASTM D2344 | ||
120.0 °C | 51 MPa Show Material materials with Shear strength, τ₁₃ of 51 MPa | ASTM D2344 | |||
150.0 °C | 45 MPa Show Material materials with Shear strength, τ₁₃ of 45 MPa | ASTM D2344 | |||
Zugfestigkeit | 23.0 °C | 910 MPa Show Material materials with Zugfestigkeit of 910 MPa | ASTM D3039 | ||
Zugfestigkeit, transversal | 23.0 °C | 881 MPa Show Material materials with Zugfestigkeit, transversal of 881 MPa | ASTM D3039 | ||
Formänderungsenergieabgabe | ASTM D5528 |
Technological properties
Property | ||
---|---|---|
Application areas | Drones;Sports equipment: Frame, wheels, seat, seat post, handlebar, head stem and crank arm of a sports bicycle are made of carbon composite;Geometry strengthen elements: Experimental stringer panel | |
Processing history | Samples for testing were obtained by vacuum infusion based on T26 resin and carbon fabric (CF) 22508 (sateen 8H, 200 g/m2, 3K, 3.95 GPa). | |
Processing methods | Preheat the resin to 60-90°С in its container for transfer to the resin pot. Degas the resin for 30-40 minutes while heating to 90°С. Preheat the tool to 100-110°С (or to 115-120°С for parts having complex shape or for UD parts). Maintaining resin pot temperature of 95 °С and tool temperature of 100-115 °С, begin resin infusion. After complete impregnation increase tool temperature at 2°С/min to 180°С. Dwell at 180°С for 3 h. Cool the tool to 90°С at <5°С/min before releasing part from tool. |