Allgemein
Property | Temperature | Value | Comment |
---|---|---|---|
Dichte | 23.0 °C | 0.94 g/cm³ Show Supplier Material materials with Dichte of 0.94 g/cm³ | ASTM D297 |
Mechanisch
Property | Temperature | Value | Comment |
---|---|---|---|
Dehnung | 23.0 °C | 420 % Show Supplier Material materials with Dehnung of 420 % | ASTM D412 |
Druckverformungsrest | 23.0 °C | 23 [-] Show Supplier Material materials with Druckverformungsrest of 23 [-] | ASTM D395, 22 h |
70.0 °C | 32 [-] Show Supplier Material materials with Druckverformungsrest of 32 [-] | ASTM D395, 22 h | |
120.0 °C | 49 [-] Show Supplier Material materials with Druckverformungsrest of 49 [-] | ASTM D395, 22 h | |
Härte, Shore A | 23.0 °C | 73 - 79 [-] Show Supplier Material materials with Härte, Shore A of 73 - 79 [-] | ASTM 2240, for 5-15 seconds |
Reißfestigkeit | 23.0 °C | 32 kN/m Show Supplier Material materials with Reißfestigkeit of 32 kN/m | ASTM D624 |
Zugfestigkeit | 23.0 °C | 7 MPa Show Supplier Material materials with Zugfestigkeit of 7 MPa | ASTM D412 |
Thermisch
Property | Value | Comment |
---|---|---|
Brittleness temperature | -60 °C Show Supplier Material materials with Brittleness temperature of -60 °C | D746 |
Technological properties
Property | ||
---|---|---|
Processing methods | Extrusion: Hopper Temperature: 140-150°C, Middle Temperature: 150-170°C, Measurment Temperature: 170-190°C, Front Temperature: 180-200°C, Mold Temperature: 170-190°C, Melt Temperature: 160-180°C, Comp. Ratio:3:1, Screen: 20-60 Mesh - Injection: Rear Temperature: 150-170°C, Middle Temperature: 170-190°C, Front Temperature: 190-220°C, Nozzle Temperature: 190-210°C, Melt Temperature:180-200°C, Mold Temperature: 30-80°C, Speed: 100-200rpm, Back Pressure 0.07 - 0.7Mpa |