Allgemein
Property | Temperature | Value | Comment |
---|---|---|---|
Dichte | 23.0 °C | 0.93 g/cm³ Show Supplier Material materials with Dichte of 0.93 g/cm³ | ASTM D297 |
Mechanisch
Property | Temperature | Value | Comment |
---|---|---|---|
Dehnung | 23.0 °C | 400 % Show Supplier Material materials with Dehnung of 400 % | ASTM D412 |
Druckverformungsrest | 23.0 °C | 38 [-] Show Supplier Material materials with Druckverformungsrest of 38 [-] | ASTM D395, 22 h |
70.0 °C | 50 [-] Show Supplier Material materials with Druckverformungsrest of 50 [-] | ASTM D395, 22 h | |
120.0 °C | 70 [-] Show Supplier Material materials with Druckverformungsrest of 70 [-] | ASTM D395, 22 h | |
Härte, Shore D | 23.0 °C | 38 - 42 [-] Show Supplier Material materials with Härte, Shore D of 38 - 42 [-] | ASTM 2240, for 5-15 seconds |
Reißfestigkeit | 23.0 °C | 70 kN/m Show Supplier Material materials with Reißfestigkeit of 70 kN/m | ASTM D624 |
Zugfestigkeit | 23.0 °C | 19 MPa Show Supplier Material materials with Zugfestigkeit of 19 MPa | ASTM D412 |
Thermisch
Property | Value | Comment |
---|---|---|
Brittleness temperature | -50 °C Show Supplier Material materials with Brittleness temperature of -50 °C | D746 |
Technological properties
Property | ||
---|---|---|
Processing methods | Extrusion: Hopper Temperature: 150-170°C, Middle Temperature: 160-180°C, Measurment Temperature: 180-200°C, Front Temperature: 190-210°C, Mold Temperature: 180-200°C, Melt Temperature: 170-190°C, Comp. Ratio:3:1, Screen: 20-60 Mesh - Injection: Rear Temperature: 130-150°C, Middle Temperature: 150-170°C, Front Temperature: 180-200°C, Nozzle Temperature: 180-190°C, Melt Temperature:160-190°C, Mold Temperature: 30-80°C, Speed: 100-200rpm, Back Pressure 0.07 - 0.7Mpa |