Allgemein
Property | Temperature | Value | Comment |
---|---|---|---|
Dichte | 23.0 °C | 0.91 g/cm³ Show Supplier Material materials with Dichte of 0.91 g/cm³ | ASTM D792 |
Mechanisch
Property | Temperature | Value | Comment |
---|---|---|---|
Dehnung | 23.0 °C | 720 % Show Supplier Material materials with Dehnung of 720 % | ASTM D412 |
Druckverformungsrest | 23.0 °C | 20 [-] Show Supplier Material materials with Druckverformungsrest of 20 [-] | ASTM D395 |
Härte, Shore A | 23.0 °C | 30 [-] Show Supplier Material materials with Härte, Shore A of 30 [-] | ASTM D2240 |
Zugfestigkeit | 23.0 °C | 3.2 MPa Show Supplier Material materials with Zugfestigkeit of 3.2 MPa | ASTM D412 |
Thermisch
Property | Value | Comment |
---|---|---|
Brittleness temperature | -65 °C Show Supplier Material materials with Brittleness temperature of -65 °C | D746 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Schmelzmassenflussrate | 10 g/10min Show Supplier Material materials with Schmelzmassenflussrate of 10 g/10min | D1238, 190°C/5kg | |
Schrumpfung | 23.0 °C | 2.1 % Show Supplier Material materials with Schrumpfung of 2.1 % | ASTM D955 |
Technological properties
Property | ||
---|---|---|
Processing methods | Extrusion: Hopper Temperature: 130-140°C, Middle Temperature: 140-160°C, Measurment Temperature: 160-180°C, Front Temperature: 170-190°C, Mold Temperature: 160-180°C, Melt Temperature: 150-170°C, Comp. Ratio:3:1, Screen: 20-60 Mesh - Injection:Rear Temperature: 130-140°C, Middle Temperature: 140-160°C, Front Temperature: 160-180°C, Nozzle Temperature: 180-190°C, Melt Temperature:170-180°C, Mold Temperature: 30-80°C, Speed: 100-200rpm, Back Pressure 0.07 - 0.7Mpa |