Allgemein
Property | Temperature | Value | Comment |
---|---|---|---|
Dichte | 23.0 °C | 1.25 g/cm³ Show Supplier Material materials with Dichte of 1.25 g/cm³ | ASTM D792 |
Mechanisch
Property | Temperature | Value | Comment |
---|---|---|---|
Dehnung | 23.0 °C | 480 % Show Supplier Material materials with Dehnung of 480 % | ASTM D412 |
Druckverformungsrest | 70.0 °C | 64 [-] Show Supplier Material materials with Druckverformungsrest of 64 [-] | ASTM D395 |
Härte, Shore A | 23.0 °C | 70 [-] Show Supplier Material materials with Härte, Shore A of 70 [-] | ASTM D2240 |
Reißfestigkeit | 23.0 °C | 35 kN/m Show Supplier Material materials with Reißfestigkeit of 35 kN/m | ASTM D624 |
Zugfestigkeit | 23.0 °C | 10.9 MPa Show Supplier Material materials with Zugfestigkeit of 10.9 MPa | ASTM D412 |
Thermisch
Technological properties
Property | ||
---|---|---|
Processing methods | Pre-drying: 60°C for 6-8 hr, Extrusion: Hopper Temperature: 130-140°C, Middle Temperature: 140-150°C, Measurment Temperature: 140-150°C, Front Temperature: 150-170°C, Mold Temperature: 150-170°C, Melt Temperature: 160°C, Comp. Ratio: 2.5:1, Screen: 20-60 Mesh - Injection: Rear Temperature: 130-140°C, Middle Temperature: 140-160°C, Front Temperature: 160-190°C, Nozzle Temperature: 170-190°C, Melt Temperature:170°C, Mold Temperature: 30-80°C, Speed: 100-200rpm, Back Pressure 0.05-05 Mpa |