Allgemein
Property | Temperature | Value | Comment |
---|---|---|---|
Dichte | 23.0 °C | 1.26 g/cm³ Show Supplier Material materials with Dichte of 1.26 g/cm³ | ASTM D792 |
Mechanisch
Property | Temperature | Value | Comment |
---|---|---|---|
Dehnung | 23.0 °C | 360 % Show Supplier Material materials with Dehnung of 360 % | ASTM D412 |
Druckverformungsrest | 70.0 °C | 61 [-] Show Supplier Material materials with Druckverformungsrest of 61 [-] | ASTM D395 |
Härte, Shore A | 23.0 °C | 85 [-] Show Supplier Material materials with Härte, Shore A of 85 [-] | ASTM D2240 |
Reißfestigkeit | 23.0 °C | 40 kN/m Show Supplier Material materials with Reißfestigkeit of 40 kN/m | ASTM D624 |
Zugfestigkeit | 23.0 °C | 13.3 MPa Show Supplier Material materials with Zugfestigkeit of 13.3 MPa | ASTM D412 |
Thermisch
Technological properties
Property | ||
---|---|---|
Processing methods | Pre-drying: 60°C for 6-8 hr, Extrusion: Hopper Temperature: 130-140°C, Middle Temperature: 140-150°C, Measurment Temperature: 140-150°C, Front Temperature: 150-170°C, Mold Temperature: 150-170°C, Melt Temperature: 160°C, Comp. Ratio: 2.5:1, Screen: 20-60 Mesh - Injection: Rear Temperature: 130-140°C, Middle Temperature: 140-160°C, Front Temperature: 160-190°C, Nozzle Temperature: 170-190°C, Melt Temperature:170°C, Mold Temperature: 30-80°C, Speed: 100-200rpm, Back Pressure 0.05-05 Mpa |