Santoprene 101-73

Want to keep this datasheet? Save it now in your required format

Description

As part of the Thermoplstic elastomer (TPE) family, Santorene™ is a thermoplastic vulcanizate (TPV) material, developed by ExxonMobil. It is a fully dynamically vulcanized ethylene propylene diene monomer (EPDM) rubber in a thermoplastic matrix of polypropylene (PP). It makes use of the properties of both rubber and PP, resulting in a high performance elastomer that shows a feel and behaviour similar to rubber, manufactured and processed as easily as plastics.
Santorene™ 101 is a soft versatile TPV that is black in colour. It exhibits good physical and chemical properties and can be processed by injection moulding, blow moulding, and extrusion. However, it is incompatible with PVC and acetal. It is shear-dependent, polyolefin-based, and recyclable. Santorene™ also has high ozone resistance and outstanding flex fatigue resistance. It is delivered as granular material. Its key features include:

High strength and flexibility
High chemical and temperature resistance
Outstanding aesthetics
Excellent sealing capacities and durability
Easy processing and design flexibility
High performance and low costs
Reduced weight and recyclability

Diese Materialdaten wurden von Matmatch zur Verfügung gestellt

Alle Daten beziehen sich auf Raumtemperatur soweit nicht anderweitig spezifiziert. SI Einheiten werden verwendt soweit nicht anderweitig spezifiziert.
Äquivalente Standards sind ähnlich zu einem oder mehreren Standards die der Anbieter angegeben hat. Manche äquivalente Standards können strikter sein oder außerhalb der Bedingungen des ursprünglichen Standards.

Ashby charts

All categories

Eigenschaften

Allgemein

Property	Temperature	Value	Comment
Dichte	23.0 °C	0.97 g/cm³ Show Material materials with Dichte of 0.97 g/cm³	ASTM D792

Mechanisch

Property	Temperature	Value	Comment
Dehnung	23.0 °C	480 % Show Material materials with Dehnung of 480 %	ASTM D412
Druckverformungsrest	70.0 °C	27 [-] Show Material materials with Druckverformungsrest of 27 [-]	ISON 815, 22 hr, Type A
Härte, Shore A	23.0 °C	78 [-] Show Material materials with Härte, Shore A of 78 [-]	ISO 868, 15 sec
Reißfestigkeit	23.0 °C	25 kN/m Show Material materials with Reißfestigkeit of 25 kN/m	ISO 34-1
Zugfestigkeit	23.0 °C	7.98 MPa Show Material materials with Zugfestigkeit of 7.98 MPa	ASTM D412

Thermisch

Property	Value	Comment
Brittleness temperature	-60 °C Show Material materials with Brittleness temperature of -60 °C	ISO 812
Relative temperature index, electrical	90 °C Show Material materials with Relative temperature index, electrical of 90 °C	UL 746
Relative temperature index, mechanical strength	90 - 95 °C Show Material materials with Relative temperature index, mechanical strength of 90 - 95 °C	UL 746, 1-3 mm
Schmelzpunkt	202 °C Show Material materials with Schmelzpunkt of 202 °C
Entflammbarkeit	HB UL94

Elektrisch

Property	Temperature	Value	Comment
Dielektrizitätskonstante	23.0 °C	2.5 [-] Show Material materials with Dielektrizitätskonstante of 2.5 [-]	ASTM D150
Durchschlagfestigkeit	23.0 °C	27 kV/mm Show Material materials with Durchschlagfestigkeit of 27 kV/mm	ASTM D149
Kriechstromfestigkeit	23.0 °C	0 V Show Material materials with Kriechstromfestigkeit of 0 V	UL 746, PLC

Technological properties

Property
Application areas	Diaphrams, Seals; Tubing, Electrical Parts, Gaskets, Automotive Applications, Outdoor Appliactions, Air Induction Systems
Color	Black
Processing methods	Blow Molding, Coextrusion, Extrusion Blow Molding, Injection Blow Molding, Sheet Extrusion, Thermoforming, Multi Injection Molding, Cacuum Forming, Profile Extruion - Extrusion: Drying Temperature: 82°C, Drying Time: 3 hr, Melt Temperature: 202°C, Die Temperature: 204°C, Back Pressure: 5-20 MPa - Injection Molding: Drying Temperature: 82°C, Drying Time: 3 hr, Rear Temperature: 177°C, Middle Temperature: 182°C, Front Temperature: 188°C, Nozzle Temperature: 193-277°C, Melt Temperature:193-277°C, Mold Temperature: 10-52°C, Back Pressure: 0.345-0.689 MPa, Screw Speed: 100-200 rpm, Screw Compression Ratio: 2:1-2.5:1

Santoprene 101-73