Allgemein
Property | Temperature | Value | Comment |
---|---|---|---|
Dichte | 23.0 °C | 0.97 g/cm³ Show Material materials with Dichte of 0.97 g/cm³ | ASTM D792 |
Mechanisch
Property | Temperature | Value | Comment |
---|---|---|---|
Dehnung | 23.0 °C | 450 % Show Material materials with Dehnung of 450 % | ASTM D412 |
Druckverformungsrest | 70.0 °C | 25 [-] Show Material materials with Druckverformungsrest of 25 [-] | ISO 185, 22 hr, Type A |
Härte, Shore A | 23.0 °C | 70 [-] Show Material materials with Härte, Shore A of 70 [-] | ISO 868, 15 sec |
Reißfestigkeit | 23.0 °C | 22.9 kN/m Show Material materials with Reißfestigkeit of 22.9 kN/m | ISO 34-1 |
Zugfestigkeit | 23.0 °C | 6.47 MPa Show Material materials with Zugfestigkeit of 6.47 MPa | ASTM D412 |
Thermisch
Property | Value | Comment | |
---|---|---|---|
Brittleness temperature | -60 °C Show Material materials with Brittleness temperature of -60 °C | ISO 812 | |
Relative temperature index, electrical | 90 °C Show Material materials with Relative temperature index, electrical of 90 °C | UL 746 | |
Relative temperature index, mechanical strength | 90 - 95 °C Show Material materials with Relative temperature index, mechanical strength of 90 - 95 °C | UL 746, 1-3 mm | |
Entflammbarkeit | HB UL94 |
Elektrisch
Property | Temperature | Value | Comment |
---|---|---|---|
Dielektrizitätskonstante | 23.0 °C | 2.5 [-] Show Material materials with Dielektrizitätskonstante of 2.5 [-] | ASTM D150 |
Durchschlagfestigkeit | 23.0 °C | 27 kV/mm Show Material materials with Durchschlagfestigkeit of 27 kV/mm | ASTM D149 |
Kriechstromfestigkeit | 23.0 °C | 0 V Show Material materials with Kriechstromfestigkeit of 0 V | UL 746, PLC |
spezifischer Widerstand | 23.0 °C | 1.00E+14 Ω·m Show Material materials with spezifischer Widerstand of 1.00E+14 Ω·m | ASTM D257, 2 mm |
Technological properties
Property | ||
---|---|---|
Application areas | Diaphrams, Seals; Tubing, Electrical Parts, Gaskets, Automotive Applications, Outdoor Appliactions, Air Induction Systems | |
Color | Black | |
Processing methods | Blow Molding, Coextrusion, Extrusion Blow Molding, Injection Blow Molding, Sheet Extrusion, Thermoforming, Multi Injection Molding, Cacuum Forming, Profile Extruion - Extrusion: Drying Temperature: 82°C, Drying Time: 3 hr, Melt Temperature: 196°C, Die Temperature: 199°C, Back Pressure: 5-20 MPa - Injection Molding: Drying Temperature: 82°C, Drying Time: 3 hr, Rear Temperature: 177°C, Middle Temperature: 182°C, Front Temperature: 182°C,Nozzle Temperature: 188-221°C, Melt Temperature: 192-232°C, Mold Temperature: 10-52°C, Back Pressure: 0.345-0.69 MPa, Screw Speed 100-200 rpm, Screw Compression Ratio: 2:1 to 2.5:1 |