Allgemein
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coefficient of friction | 0.35 - 0.45 [-] Show Material materials with Coefficient of friction of 0.35 - 0.45 [-] | ISO 7148-2 | |
Dichte | 23.0 °C | 1.15 g/cm³ Show Material materials with Dichte of 1.15 g/cm³ | ISO 1183-1 |
Wasserabsorption | 23.0 °C | 0.68 % Show Material materials with Wasserabsorption of 0.68 % | ISO 62 |
Wasseraufnahme, Sättigung | 23.0 °C | 7.8 % Show Material materials with Wasseraufnahme, Sättigung of 7.8 % |
Mechanisch
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Biegefestigkeit | 23.0 °C | 128 MPa Show Material materials with Biegefestigkeit of 128 MPa | ISO 178 | ||
Biegemodul | 23.0 °C | 3.2 GPa Show Material materials with Biegemodul of 3.2 GPa | ISO 178 | ||
Dehnung | 23.0 °C | 20 % Show Material materials with Dehnung of 20 % | ISO 527-1/-2 | ||
Druckverformungsrest | 23.0 °C | 32 - 100 [-] Show Material materials with Druckverformungsrest of 32 - 100 [-] | For 1-5 nominal strain | ||
Elastizitätsmodul | 23.0 °C | 3.6 GPa Show Material materials with Elastizitätsmodul of 3.6 GPa | ISO 527-1, ISO 527-2 | ||
Elongation at yield | 23.0 °C | 5 % Show Material materials with Elongation at yield of 5 % | ISO 527-1, ISO 527-2 | ||
Härte, Rockwell M | 23.0 °C | 88 [-] Show Material materials with Härte, Rockwell M of 88 [-] | ISO 2039-2 | ||
Zugfestigkeit | 23.0 °C | 95 MPa Show Material materials with Zugfestigkeit of 95 MPa | ISO 527-1/-2 | ||
Schlagzähigkeit, Charpy ungekerbt | No break; ISO 179-1/1eU | ||||
Thermisch
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Heat deflection temperature, 1.80 MPa | 85 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 85 °C | ISO 75-1/-2 | |||
Koeffizient der thermischen Ausdehnung | 60.0 °C | 8E-5 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 8E-5 1/K | Average value between 23°C and the mentioned Temperature | ||
100.0 °C | 9E-5 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 9E-5 1/K | Average value between 23°C and the mentioned Temperature | |||
Max. Betriebstemperatur | 80 °C Show Material materials with Max. Betriebstemperatur of 80 °C | For min. 20,000 h | |||
Min. Betriebstemperatur | -20 °C Show Material materials with Min. Betriebstemperatur of -20 °C | ||||
Schmelzpunkt | 260 °C Show Material materials with Schmelzpunkt of 260 °C | ISO 11357-1/-3 | |||
Entflammbarkeit | UL 94 (3 mm thickness) HB | ||||
Elektrisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dielektrizitätskonstante | 23.0 °C | 3.3 [-] Show Material materials with Dielektrizitätskonstante of 3.3 [-] | IEC 60250, at 1MHz |
Durchschlagfestigkeit | 23.0 °C | 26 kV/mm Show Material materials with Durchschlagfestigkeit of 26 kV/mm | IEC 60243-1 |
Surface resistivity | 23.0 °C | 1.00E+13 Ω/sq Show Material materials with Surface resistivity of 1.00E+13 Ω/sq | ANIS/ESD STM 11.11 |
spezifischer Widerstand | 23.0 °C | 1.00E+12 Ω·m Show Material materials with spezifischer Widerstand of 1.00E+12 Ω·m | IEC 60093 |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Gears, Sprockets, Star wheels, Bushings, Bearings, Wear Pads, Rails and Strips, Pulleys, Sheaves andGuides, Conveyor Wheels, Rollers and Sleeves, Supports Blocks, Valve Seats, Valve seals | |
| Color | Grey | |
| Fillers | Molybdenum disulfide (MoS2) | |