Allgemein
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dichte | 23.0 °C | 1.19 g/cm³ Show Material materials with Dichte of 1.19 g/cm³ | ASTM D 792 |
Wasseraufnahme, Gleichgewicht | 100.0 °C | 0.58 % Show Material materials with Wasseraufnahme, Gleichgewicht of 0.58 % | ASTM D 570 | ASTM D 570 |
Mechanisch
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Biegemodul | 23.0 °C | 2.34 GPa Show Material materials with Biegemodul of 2.34 GPa | ASTM D 790 | 1.3 mm/min, 50 mm span | ||
Flexural yield strength | 23.0 °C | 97 MPa Show Material materials with Flexural yield strength of 97 MPa | ASTM D 790 | 1.3 mm/min, 50 mm span | ||
Impact strength, Izod notched, ASTM | 23.0 °C | 907 J/m Show Material materials with Impact strength, Izod notched, ASTM of 907 J/m | ASTM D 256 | ||
Streckgrenze | 23.0 °C | 62 MPa Show Material materials with Streckgrenze of 62 MPa | ASTM D 638 | Type I, 50 mm/min | ||
Zugfestigkeit | 23.0 °C | 68 MPa Show Material materials with Zugfestigkeit of 68 MPa | ASTM D 638 | Type I, 50 mm/min | ||
Impact strength, Izod unnotched, ASTM | No break @ 23°C | ASTM D 4812 | ||||
Thermisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Heat deflection temperature, 1.80 MPa | 132 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 132 °C | ASTM D 648 | 1.82 MPa, 6.4 mm, unannealed | |
Koeffizient der thermischen Ausdehnung | 23.0 °C | 6.84E-5 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 6.84E-5 1/K | ASTM E 831 | -40°C to 95°C |
Vicat-Erweichungstemperatur | 154 °C Show Material materials with Vicat-Erweichungstemperatur of 154 °C | ASTM D 1525 | Rate B/50 |
Optisch
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Schmelzmassenflussrate | 7 g/10min Show Material materials with Schmelzmassenflussrate of 7 g/10min | ASTM D 1238 | 300°C/1.2 kg | |
Schrumpfung | 23.0 °C | 0.5 - 0.7 % Show Material materials with Schrumpfung of 0.5 - 0.7 % | SABIC method | 3.2 mm |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Building/Construction Sheet | |
| Processing methods | Drying Temperature: 120°C, Drying Time: 3-4hrs, Drying Time (Cumulative): 48hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 310-330°C, Nozzle Temperature: 305-325°C, Front - Zone 3 Temperature: 310-330°C, Middle - Zone 2 Temperature: 300-320°C, Rear - Zone 1 Temperature: 290-310°C, Mold Temperature: 80-115°C, Back Pressure: 0.3-0.7MPa, Screw Speed: 40-70rpm, Shot to Cylinder Size: 40-60%, Vent Depth: 0.025-0.076mm | |