Allgemein
Property | Temperature | Value | Comment |
---|---|---|---|
Dichte | 23.0 °C | 1.62 g/cm³ Show Material materials with Dichte of 1.62 g/cm³ | ASTM D 792 |
Wasserabsorption | 23.0 °C | 0.07 % Show Material materials with Wasserabsorption of 0.07 % | ISO 62 | 23°C, 50% RH |
Mechanisch
Property | Temperature | Value | Comment |
---|---|---|---|
Biegefestigkeit | 23.0 °C | 130 MPa Show Material materials with Biegefestigkeit of 130 MPa | ISO 178 |
Biegemodul | 23.0 °C | 8.3 GPa Show Material materials with Biegemodul of 8.3 GPa | ISO 178 | 2 mm/min |
Dehnung | 23.0 °C | 2 % Show Material materials with Dehnung of 2 % | ASTM D 638 | Type I, 5 mm/min |
Elastizitätsmodul | 23.0 °C | 10.4 GPa Show Material materials with Elastizitätsmodul of 10.4 GPa | ASTM D 638 | 5 mm/min |
Elongation at yield | 23.0 °C | 2 % Show Material materials with Elongation at yield of 2 % | ASTM D 638 | Type I, 5 mm/min |
Flexural strain | 23.0 °C | 2 % Show Material materials with Flexural strain of 2 % | ISO 178 | 2 mm/min |
Flexural yield strength | 23.0 °C | 130 MPa Show Material materials with Flexural yield strength of 130 MPa | ISO 178 | 2 mm/min |
Hardness, Ball Indentation | 23.0 °C | 144 MPa Show Material materials with Hardness, Ball Indentation of 144 MPa | ISO 2039-1 |
Hardness, Rockwell R | 23.0 °C | 124 [-] Show Material materials with Hardness, Rockwell R of 124 [-] | ISO 2039-2 |
Impact strength, Izod notched, ASTM | -30.0 °C | 50 J/m Show Material materials with Impact strength, Izod notched, ASTM of 50 J/m | ASTM D 256 |
23.0 °C | 60 J/m Show Material materials with Impact strength, Izod notched, ASTM of 60 J/m | ASTM D 256 | |
Impact strength, Izod unnotched, ASTM | -30.0 °C | 520 J/m Show Material materials with Impact strength, Izod unnotched, ASTM of 520 J/m | ASTM D 4812 |
23.0 °C | 560 J/m Show Material materials with Impact strength, Izod unnotched, ASTM of 560 J/m | ASTM D 4812 | |
Schlagfestigkeit, Charpy gekerbt | -30.0 °C | 7 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 7 kJ/m² | ISO 179/2C |
23.0 °C | 7 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 7 kJ/m² | ISO 179/2C | |
Schlagzähigkeit, Charpy ungekerbt | -30.0 °C | 30 kJ/m² Show Material materials with Schlagzähigkeit, Charpy ungekerbt of 30 kJ/m² | ISO 179/1eU |
23.0 °C | 35 kJ/m² Show Material materials with Schlagzähigkeit, Charpy ungekerbt of 35 kJ/m² | ISO 179/1eU | |
Schlagzähigkeit, Izod gekerbt | -30.0 °C | 5 kJ/m² Show Material materials with Schlagzähigkeit, Izod gekerbt of 5 kJ/m² | ISO 180/1A |
23.0 °C | 5 kJ/m² Show Material materials with Schlagzähigkeit, Izod gekerbt of 5 kJ/m² | ISO 180/1A | |
Schlagzähigkeit, Izod ungekerbt | -30.0 °C | 25 kJ/m² Show Material materials with Schlagzähigkeit, Izod ungekerbt of 25 kJ/m² | ISO 180/1U |
23.0 °C | 35 kJ/m² Show Material materials with Schlagzähigkeit, Izod ungekerbt of 35 kJ/m² | ISO 180/1U | |
Streckgrenze | 23.0 °C | 95 MPa Show Material materials with Streckgrenze of 95 MPa | ASTM D 638 | Type I, 5 mm/min |
Zugfestigkeit | 23.0 °C | 95 MPa Show Material materials with Zugfestigkeit of 95 MPa | ASTM D 638 | Type I, 5 mm/min |
Thermisch
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Heat deflection temperature, 0.45 MPa | 215 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 215 °C | ISO 75/Bf | 0.45 MPa | |||
Koeffizient der thermischen Ausdehnung | 23.0 °C | 2.18E-5 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 2.18E-5 1/K | ISO 11359-2 | 23°C to 150°C | ||
Relative temperature index, electrical | 140 °C Show Material materials with Relative temperature index, electrical of 140 °C | UL 746B | |||
Relative temperature index, mechanical impact | 140 °C Show Material materials with Relative temperature index, mechanical impact of 140 °C | UL 746B | |||
Relative temperature index, mechanical strength | 140 °C Show Material materials with Relative temperature index, mechanical strength of 140 °C | UL 746B | |||
Vicat-Erweichungstemperatur | 185 °C Show Material materials with Vicat-Erweichungstemperatur of 185 °C | ASTM D 1525 | Rate B/50 | |||
Wärmeleitfähigkeit | 23.0 °C | 0.36 W/(m·K) Show Material materials with Wärmeleitfähigkeit of 0.36 W/(m·K) | ISO 8302 | ||
thermischer Ausdehnungskoeffizient, transversal | 23.0 °C | 1.4E-4 1/K Show Material materials with thermischer Ausdehnungskoeffizient, transversal of 1.4E-4 1/K | ISO 11359-2 | 23°C to 150°C | ||
Entflammbarkeit | UL Recognized, 94HB Flame Class Rating 2nd value | 3mm | UL 94 |
Elektrisch
Property | Temperature | Value | Comment |
---|---|---|---|
Dielektrizitätskonstante | 23.0 °C | 3.5 [-] Show Material materials with Dielektrizitätskonstante of 3.5 [-] | IEC 60250 | at 50/60 Hz |
Durchschlagfestigkeit | 23.0 °C | 18 kV/mm Show Material materials with Durchschlagfestigkeit of 18 kV/mm | ASTM D 149 | in oil, 3.2 mm |
Kriechstromfestigkeit | 23.0 °C | 2 V Show Material materials with Kriechstromfestigkeit of 2 V | UL 746A |
Verlustfaktor | 23.0 °C | 0.02 [-] Show Material materials with Verlustfaktor of 0.02 [-] | IEC 60250 | at 1 MHz |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Melt viscosity | 260.0 °C | 160 Pa·s Show Material materials with Melt viscosity of 160 Pa·s | ISO 11443 | 1500 sec⁻¹ |
Schmelzmassenflussrate | 20 g/10min Show Material materials with Schmelzmassenflussrate of 20 g/10min | ASTM D 1238 | 266°C/5.0 kg | |
Schmelzvolumenflussrate | 15 cm³/10min Show Material materials with Schmelzvolumenflussrate of 15 cm³/10min | ISO 1133 | 265°C/5.0 kg | |
Schrumpfung | 23.0 °C | 0.3 - 0.6 % Show Material materials with Schrumpfung of 0.3 - 0.6 % | SABIC method |
Schrumpfung, diagonal | 23.0 °C | 0.5 - 0.8 % Show Material materials with Schrumpfung, diagonal of 0.5 - 0.8 % | SABIC method |
Technological properties
Property | ||
---|---|---|
Application areas | Electronic Components,Enclosures,Exterior Mirror,Medical Device,Pump,Wiring Devices | |
Fillers | 40% Glass Fiber and Mineral Powder | |
Processing methods | Drying Temperature: 110-120°C, Drying Time: 4-6hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 260-285°C, Nozzle Temperature: 265-275°C, Front - Zone 3 Temperature: 260-280°C, Middle - Zone 2 Temperature: 255-280°C, Rear - Zone 1 Temperature: 240-260°C, Hopper Temperature: 40-60°C, Mold Temperature: 60-110°C |