Allgemein
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dichte | 23.0 °C | 1.46 g/cm³ Show Material materials with Dichte of 1.46 g/cm³ | ASTM D 792 |
Wasserabsorption | 23.0 °C | 0.09 % Show Material materials with Wasserabsorption of 0.09 % | ASTM D 570 | 24 Hours |
Mechanisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Biegemodul | 23.0 °C | 3.44 GPa Show Material materials with Biegemodul of 3.44 GPa | ASTM D 790 | 1.3 mm/min, 50 mm span |
Flexural yield strength | 23.0 °C | 89 MPa Show Material materials with Flexural yield strength of 89 MPa | ASTM D 790 | 1.3 mm/min, 50 mm span |
Hardness, Rockwell R | 23.0 °C | 112 [-] Show Material materials with Hardness, Rockwell R of 112 [-] | ASTM D 785 |
Impact strength, Izod notched, ASTM | 23.0 °C | 80 J/m Show Material materials with Impact strength, Izod notched, ASTM of 80 J/m | ASTM D 256 |
Impact strength, Izod unnotched, ASTM | 23.0 °C | 1602 J/m Show Material materials with Impact strength, Izod unnotched, ASTM of 1602 J/m | ASTM D 4812 |
Streckgrenze | 23.0 °C | 48 MPa Show Material materials with Streckgrenze of 48 MPa | ASTM D 638 | Type I, 50 mm/min |
Zugfestigkeit | 23.0 °C | 46 MPa Show Material materials with Zugfestigkeit of 46 MPa | ASTM D 638 | Type I, 50 mm/min |
Thermisch
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Heat deflection temperature, 1.80 MPa | 87 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 87 °C | ASTM D 648 | 1.82 MPa, 6.4 mm, unannealed | |||
Koeffizient der thermischen Ausdehnung | 23.0 °C | 1.39E-4 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 1.39E-4 1/K | ASTM E 831 | 60°C to 138°C | ||
Relative temperature index, electrical | 105 °C Show Material materials with Relative temperature index, electrical of 105 °C | UL 746B | |||
Relative temperature index, mechanical impact | 105 °C Show Material materials with Relative temperature index, mechanical impact of 105 °C | UL 746B | |||
Relative temperature index, mechanical strength | 105 °C Show Material materials with Relative temperature index, mechanical strength of 105 °C | UL 746B | |||
Entflammbarkeit | UL Recognized, 94HB Flame Class Rating | 1.47mm | UL 94 | ||||
Elektrisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dielektrizitätskonstante | 23.0 °C | 3.2 [-] Show Material materials with Dielektrizitätskonstante of 3.2 [-] | ASTM D 150 | at 1 MHz |
Durchschlagfestigkeit | 23.0 °C | 24.8 kV/mm Show Material materials with Durchschlagfestigkeit of 24.8 kV/mm | ASTM D 149 | in oil, 1.6 mm |
Kriechstromfestigkeit | 23.0 °C | 2 V Show Material materials with Kriechstromfestigkeit of 2 V | UL 746A |
Verlustfaktor | 23.0 °C | 0.01 [-] Show Material materials with Verlustfaktor of 0.01 [-] | ASTM D 150 | at 1 MHz |
spezifischer Widerstand | 23.0 °C | 6.90E+14 Ω·m Show Material materials with spezifischer Widerstand of 6.90E+14 Ω·m | ASTM D 257 |
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Schrumpfung | 23.0 °C | 0.6 - 0.8 % Show Material materials with Schrumpfung of 0.6 - 0.8 % | SABIC method | 1.5-3.2 mm |
Schrumpfung, diagonal | 23.0 °C | 0.6 - 0.8 % Show Material materials with Schrumpfung, diagonal of 0.6 - 0.8 % | SABIC method | 1.5-3.2 mm |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Displays,Electronic Components,Enclosures,Heavy Vehicles,Medical Device,Medical Facility Infrastructure,Security/Detection | |
| Fillers | 30% Mineral Powder | |
| Processing methods | Drying Temperature: 120°C, Drying Time: 3-4hrs, Drying Time (Cumulative): 12hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 255-275°C, Nozzle Temperature: 255-270°C, Front - Zone 3 Temperature: 255-265°C, Middle - Zone 2 Temperature: 250-260°C, Rear - Zone 1 Temperature: 245-255°C, Mold Temperature: 65-95°C, Back Pressure: 0.3-0.7MPa, Screw Speed: 50-80rpm, Shot to Cylinder Size: 40-80%, Vent Depth: 0.025-0.038mm | |